SABIC Innovative Plastics LNP LUBRICOMP DFL22 PC (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP DFL22 PC (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* DFL22 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Physical Properties Metric English Comments
Density 1.33 g/cc
0.0480 lb/in³
ISO 1183
1.34 g/cc
0.0484 lb/in³
ASTM D792
Moisture Absorption 0.100 %
0.100 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Time 86400 sec
 0.0040 - 0.0060 in/in

@Time 24.0 hour
 ASTM D955
0.0050 cm/cm

@Time 86400 sec
 0.0050 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.0065 cm/cm

@Time 86400 sec
 0.0065 in/in

@Time 24.0 hour
 ISO 294
0.0060 - 0.0080 cm/cm

@Time 86400 sec
 0.0060 - 0.0080 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 67.0 MPa
9720 psi
ASTM D638
67.0 MPa
9720 psi
ISO 527
67.0 MPa
9720 psi
5 mm/min; ISO 527
68.0 MPa
9860 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 71.0 MPa
10300 psi
ASTM D638
71.0 MPa
10300 psi
ISO 527
71.0 MPa
10300 psi
5 mm/min; ISO 527
72.0 MPa
10400 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 5.5 %
5.5 %
ASTM D638
5.5 %
5.5 %
Type I, 5 mm/min; ASTM D638
5.8 %
5.8 %
ISO 527
5.8 %
5.8 %
5 mm/min; ISO 527
Elongation at Yield 3.3 %
3.3 %
ASTM D638
3.3 %
3.3 %
ISO 527
3.3 %
3.3 %
5 mm/min; ISO 527
3.5 %
3.5 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 4.13 GPa
599 ksi
50 mm/min; ASTM D638
4.15 GPa
602 ksi
1 mm/min; ISO 527
Flexural Strength 118 MPa
17100 psi
ISO 178
Flexural Yield Strength 118 MPa
17100 psi
2 mm/min; ISO 178
Flexural Modulus 3.90 GPa
566 ksi
ISO 178
3.90 GPa
566 ksi
2 mm/min; ISO 178
4.13 GPa
599 ksi
ASTM D790
4.14 GPa
600 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 1.44 J/cm
2.70 ft-lb/in
ASTM D256
Izod Impact, Unnotched 7.36 J/cm
13.8 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 13.0 kJ/m²
6.19 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 48.0 kJ/m²
22.8 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 23.0 J
17.0 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 6.00 J
4.43 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.37
0.37
ASTM D3702 Modified
Coefficient of Friction, Static 0.43
0.43
ASTM D3702 Modified
K (wear) Factor 332 x 10-8 mm³/N-M
165 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 55.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
 31.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
56.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 31.1 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
56.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 31.1 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 55.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
 31.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
56.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 31.1 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
56.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 31.1 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 146 °C
295 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
145 °C

@Thickness 3.20 mm
 293 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 140 °C
284 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
140 °C

@Thickness 3.20 mm
 284 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Users viewing this material also viewed the following: