SABIC Innovative Plastics LNP LUBRICOMP DFL14 PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP DFL14 PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRICOMP* DFL14 is a compound based on Polycarbonate resin containing 20% Glass Fiber and 5% PTFE. Added features include: Internally Lubricated.
Physical Properties Metric English Comments
Specific Gravity 1.38 g/cc
1.38 g/cc
ASTM D792
Density 1.38 g/cc
0.0499 lb/in³
ASTM D792
Moisture Absorption 0.120 %
0.120 %
50% RH, 24 hrs; ASTM D570
0.190 %
0.190 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm

@Time 86400 sec
0.0020 - 0.0040 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm

@Time 86400 sec
0.0050 - 0.0070 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 94.0 MPa
13600 psi
Type I, 5 mm/min; ASTM D638
94.0 MPa
13600 psi
5 mm/min; ISO 527
Tensile Strength, Yield 96.0 MPa
13900 psi
Type I, 5 mm/min; ASTM D638
96.0 MPa
13900 psi
5 mm/min; ISO 527
Elongation at Break 3.5 %
3.5 %
5 mm/min; ISO 527
3.8 %
3.8 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 2.9 %
2.9 %
5 mm/min; ISO 527
3.0 %
3.0 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 6.02 GPa
873 ksi
1 mm/min; ISO 527
6.32 GPa
917 ksi
5 mm/min; ASTM D638
Flexural Strength 158 MPa
22900 psi
ISO 178
161 MPa
23400 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Yield Strength 165 MPa
23900 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 5.59 GPa
811 ksi
2 mm/min; ISO 178
5.82 GPa
844 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 1.70 J/cm
3.18 ft-lb/in
ASTM D256
Izod Impact, Unnotched 7.16 J/cm
13.4 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 15.0 kJ/m²
7.14 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 54.0 kJ/m²
25.7 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 23.0 J

@Temperature 23.0 °C
17.0 ft-lb

@Temperature 73.4 °F
ASTM D3763
Impact Test 5.00 J
3.69 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.44
0.44
ASTM D3702 Modified
Coefficient of Friction, Static 0.53
0.53
ASTM D3702 Modified
K (wear) Factor 22.2 x 10-8 mm³/N-M
11.0 x 10-10 in³-min/ft-lb-hr
Ring; ASTM D3702 Modified
318 x 10-8 mm³/N-M
158 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 25.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
13.9 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
CTE, linear, Transverse to Flow 41.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
22.8 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 145 °C
293 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
146 °C

@Thickness 3.20 mm
295 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 141 °C
286 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
142 °C

@Thickness 3.20 mm
288 °F

@Thickness 0.126 in
unannealed; ASTM D648