SABIC Innovative Plastics LNP LUBRICOMP Cycoloy_C6303 PC+ABS

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP Cycoloy_C6303 PC+ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* Cycoloy_C6303 compound is a Wear resistant (5% PTFE), flame retardant PC+ABS. High heat and good hydrolytic stability. UL listing from Japan and Pacific.
Physical Properties Metric English Comments
Specific Gravity 1.25 g/cc
1.25 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0060 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 10 g/10 min

@Load 2.16 kg,
Temperature 260 °C
 10 g/10 min

@Load 4.76 lb,
Temperature 500 °F
 ASTM D1238
50 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 50 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.0 MPa
7250 psi
50 mm/min; ISO 527
51.0 MPa
7400 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 65.0 MPa
9430 psi
50 mm/min; ISO 527
65.0 MPa
9430 psi
Type I, 50 mm/min; ASTM D638
100 MPa
14500 psi
5 mm/min; ISO 527
Elongation at Break 22 %
22 %
50 mm/min; ISO 527
30 %
30 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 4.5 %
4.5 %
Type I, 50 mm/min; ASTM D638
4.6 %
4.6 %
50 mm/min; ISO 527
6.0 %
6.0 %
5 mm/min; ISO 527
Tensile Modulus 2.68 GPa
389 ksi
50 mm/min; ASTM D638
2.87 GPa
416 ksi
1 mm/min; ISO 527
Flexural Yield Strength 106 MPa
15400 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.60 GPa
377 ksi
2 mm/min; ISO 178
2.75 GPa
399 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.960 J/cm
1.80 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
80*10*4; ISO 180/1A
Dart Drop, Total Energy 48.0 J

@Temperature 23.0 °C
 35.4 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 63.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 35.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
65.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 36.1 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 63.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 35.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
68.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 37.8 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 109 °C

@Thickness 3.20 mm
 228 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 92.0 °C

@Thickness 3.20 mm
 198 °F

@Thickness 0.126 in
 unannealed; ASTM D648
102 °C

@Thickness 6.40 mm
 216 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 117 °C
243 °F
Rate B/120; ISO 306
117 °C
243 °F
Rate B/50; ASTM D1525
UL RTI, Electrical 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical with Impact 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical without Impact 60.0 °C
140 °F
UL 746B
Flammability, UL94 V-1

@Thickness 1.19 mm
 V-1

@Thickness 0.0469 in
 UL 94
V-0

@Thickness 1.49 mm
 V-0

@Thickness 0.0587 in
 UL 94
5VB

@Thickness 2.48 mm
 5VB

@Thickness 0.0976 in
 UL 94
Electrical Properties Metric English Comments
Hot Wire Ignition, HWI 15 - 30 sec
15 - 30 sec
UL 746A
High Amp Arc Ignition, HAI 60 - 120 arcs
60 - 120 arcs
UL 746A