Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

SABIC Innovative Plastics LNP KONDUIT PX08322 PA 6 (Asia Pacific)

Category Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Konduit
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP KONDUIT PX08322 PA 6 (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Thermally conductive mineral filled PA6 FR compound
Physical Properties Metric English Comments
Density 1.52 g/cc
0.0549 lb/in³
ASTM D792
Water Absorption 0.39 %

@Time 86400 sec
 0.39 %

@Time 24.0 hour
 SABIC Method
Moisture Absorption 0.0600 %
0.0600 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0050 cm/cm

@Time 86400 sec
 0.0050 in/in

@Time 24.0 hour
 ASTM D955
Linear Mold Shrinkage, Transverse 0.0045 cm/cm

@Time 86400 sec
 0.0045 in/in

@Time 24.0 hour
 ASTM D955
Melt Flow 15.3 g/10 min

@Load 6.70 kg,
Temperature 285 °C
 15.3 g/10 min

@Load 14.8 lb,
Temperature 545 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 54.0 MPa
7830 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 0.70 %
0.70 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 11.79 GPa
1710 ksi
50 mm/min; ASTM D638
Flexural Strength 82.0 MPa
11900 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 11.7 GPa
1700 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.170 J/cm
0.318 ft-lb/in
ASTM D256
Izod Impact, Unnotched 0.880 J/cm
1.65 ft-lb/in
ASTM D4812
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 21.5 µm/m-°C

@Temperature -40.0 - 40.0 °C
 11.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
27.1 µm/m-°C

@Temperature 40.0 - 120 °C
 15.1 µin/in-°F

@Temperature 104 - 248 °F
 ASTM E 831
CTE, linear, Transverse to Flow 35.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
 19.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
58.3 µm/m-°C

@Temperature 40.0 - 120 °C
 32.4 µin/in-°F

@Temperature 104 - 248 °F
 ASTM E 831
Thermal Conductivity 0.920 W/m-K
6.38 BTU-in/hr-ft²-°F
through-plane, ø80*3mm discs; ISO 22007-2
2.10 W/m-K
14.6 BTU-in/hr-ft²-°F
through-plane, 10*10*3mm sample; ASTM E 1461-07
5.09 W/m-K
35.3 BTU-in/hr-ft²-°F
in-plane, ø80*3mm discs; ISO 22007-2
8.10 W/m-K
56.2 BTU-in/hr-ft²-°F
in-plane, ø25*0.4mm disc; ASTM E 1461-07
Deflection Temperature at 1.8 MPa (264 psi) 180 °C

@Thickness 6.40 mm
 356 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Flammability, UL94 V-0

@Thickness 1.20 mm
 V-0

@Thickness 0.0472 in
 UL 94
Glow Wire Test 825 °C
1520 °F
IEC 60695-2-13
960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 IEC 60695-2-12
Electrical Properties Metric English Comments
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ASTM D257
Dielectric Constant 4.8

@Frequency 1.00e+6 Hz
 4.8

@Frequency 1.00e+6 Hz
 ASTM D150
7.27

@Frequency 50.0 - 60.0 Hz
 7.27

@Frequency 50.0 - 60.0 Hz
 ASTM D150
Dielectric Strength 14.1 kV/mm

@Thickness 1.00 mm
 358 kV/in

@Thickness 0.0394 in
 in oil; ASTM D149
Dissipation Factor 0.043

@Frequency 1.00e+6 Hz
 0.043

@Frequency 1.00e+6 Hz
 ASTM D150
0.083

@Frequency 50.0 - 60.0 Hz
 0.083

@Frequency 50.0 - 60.0 Hz
 ASTM D150
Comparative Tracking Index 575 V
575 V
IEC 60112
Hot Wire Ignition, HWI >= 120 sec
>= 120 sec
UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
UL 746A
Descriptive Properties Value Comments
Water Immersion, Start F1 from 1mm onward PASSES
UL 746C
PASSES
UL 746C
Users viewing this material also viewed the following: