SABIC Innovative Plastics LNP KONDUIT PX08321 PA 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Konduit |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP KONDUIT PX08321 PA 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Konduit* PX08321 a compound based on PA6 resins containing mineral. Added features include: Thermally Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.61 g/cc | 0.0582 lb/in³ | ASTM D792 |
| Water Absorption | 0.34 % @Time 86400 sec |
0.34 % @Time 24.0 hour |
SABIC Method |
| Moisture Absorption | 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0046 cm/cm @Time 86400 sec |
0.0046 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0039 cm/cm @Time 86400 sec |
0.0039 in/in @Time 24.0 hour |
ASTM D955 |
| Melt Flow | 12.2 g/10 min @Load 6.70 kg, Temperature 285 °C |
12.2 g/10 min @Load 14.8 lb, Temperature 545 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa | 10200 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 0.90 % | 0.90 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 13.82 GPa | 2004 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 104 MPa | 15100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 14.2 GPa | 2060 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.240 J/cm | 0.450 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 1.57 J/cm | 2.94 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 16.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
9.06 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 36.3 µm/m-°C @Temperature 40.0 - 120 °C |
20.2 µin/in-°F @Temperature 104 - 248 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 28.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 55.6 µm/m-°C @Temperature 40.0 - 120 °C |
30.9 µin/in-°F @Temperature 104 - 248 °F |
ASTM E 831 | |
| Thermal Conductivity | 1.10 W/m-K | 7.63 BTU-in/hr-ft²-°F | through-plane, ø80*3mm discs; ISO 22007-2 |
| 2.60 W/m-K | 18.0 BTU-in/hr-ft²-°F | through-plane, 10*10*3mm sample; ASTM E 1461-07 | |
| 8.57 W/m-K | 59.5 BTU-in/hr-ft²-°F | in-plane, ø80*3mm discs; ISO 22007-2 | |
| 10.0 W/m-K | 69.4 BTU-in/hr-ft²-°F | in-plane, ø25*0.4mm disc; ASTM E 1461-07 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C @Thickness 3.20 mm |
378 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.00 mm |
HB @Thickness 0.0394 in |
UL 94 |
| Glow Wire Test | 825 °C | 1520 °F | IEC 60695-2-13 |
| 960 °C @Thickness 1.00 mm |
1760 °F @Thickness 0.0394 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 4.1 @Frequency 1.00e+6 Hz |
4.1 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 6.2 @Frequency 50.0 - 60.0 Hz |
6.2 @Frequency 50.0 - 60.0 Hz |
ASTM D150 | |
| Dielectric Strength | 14.7 kV/mm @Thickness 1.00 mm |
373 kV/in @Thickness 0.0394 in |
in oil; ASTM D149 |
| Dissipation Factor | 0.044 @Frequency 1.00e+6 Hz |
0.044 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 0.076 @Frequency 50.0 - 60.0 Hz |
0.076 @Frequency 50.0 - 60.0 Hz |
ASTM D150 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |