- SABIC Innovative Plastics LNP KONDUIT PX08321 PA 6 (Europe-Africa-Middle East)
SABIC Innovative Plastics LNP KONDUIT PX08321 PA 6 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Konduit |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP KONDUIT PX08321 PA 6 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Thermally conductive mineral filled PA6 compound
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.61 g/cc | 0.0582 lb/in³ | ISO 1183 |
| Water Absorption | 0.34 % @Time 86400 sec |
0.34 % @Time 24.0 hour |
SABIC Method |
| Moisture Absorption | 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0019 cm/cm @Time 86400 sec |
0.0019 in/in @Time 24.0 hour |
ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.0021 cm/cm @Time 86400 sec |
0.0021 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 59.0 MPa | 8560 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 0.80 % | 0.80 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 12.8 GPa | 1860 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 13.2 GPa | 1910 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 16.6 µm/m-°C @Temperature -30.0 - 80.0 °C |
9.22 µin/in-°F @Temperature -22.0 - 176 °F |
ISO 11359-2 |
| 19.7 µm/m-°C @Temperature 23.0 - 80.0 °C |
10.9 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 44.8 µm/m-°C @Temperature -30.0 - 80.0 °C |
24.9 µin/in-°F @Temperature -22.0 - 176 °F |
ISO 11359-2 |
| 55.1 µm/m-°C @Temperature 23.0 - 80.0 °C |
30.6 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| Thermal Conductivity | 1.10 W/m-K | 7.63 BTU-in/hr-ft²-°F | through-plane, ø80*3mm discs; ISO 22007-2 |
| 2.60 W/m-K | 18.0 BTU-in/hr-ft²-°F | through-plane, 10*10*3mm sample; ASTM E 1461-07 | |
| 8.57 W/m-K | 59.5 BTU-in/hr-ft²-°F | in-plane, ø80*3mm discs; ISO 22007-2 | |
| 10.0 W/m-K | 69.4 BTU-in/hr-ft²-°F | in-plane, ø25*0.4mm disc; ASTM E 1461-07 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 184 °C | 363 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Flammability, UL94 | HB @Thickness 1.00 mm |
HB @Thickness 0.0394 in |
UL 94 |
| Glow Wire Test | 825 °C | 1520 °F | IEC 60695-2-13 |
| 960 °C @Thickness 1.00 mm |
1760 °F @Thickness 0.0394 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 4.1 @Frequency 1.00e+6 Hz |
4.1 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 6.2 @Frequency 50.0 - 60.0 Hz |
6.2 @Frequency 50.0 - 60.0 Hz |
ASTM D150 | |
| Dielectric Strength | 14.7 kV/mm @Thickness 1.00 mm |
373 kV/in @Thickness 0.0394 in |
in oil; ASTM D149 |
| Dissipation Factor | 0.044 @Frequency 1.00e+6 Hz |
0.044 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 0.076 @Frequency 50.0 - 60.0 Hz |
0.076 @Frequency 50.0 - 60.0 Hz |
ASTM D150 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |