SABIC Innovative Plastics LNP Faradex MS003XXC PP (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP FARADEX
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Faradex MS003XXC PP (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Faradex* MS003XXC is a compound based on Polypropylene resin containing Stainless Steel Fiber. Added features of this material include: EMI/RFI Shielding.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Density 1.01 g/cc
0.0365 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.013 - 0.017 cm/cm
0.013 - 0.017 in/in
on tensile bar; SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 16.0 MPa
2320 psi
50 mm/min; ISO 527
Tensile Strength, Yield 21.0 MPa
3050 psi
50 mm/min; ISO 527
Elongation at Yield 6.3 %
6.3 %
50 mm/min; ISO 527
Tensile Modulus 1.20 GPa
174 ksi
1 mm/min; ISO 527
Flexural Modulus 1.20 GPa
174 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 19.0 kJ/m²

@Temperature 23.0 °C
9.04 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 110 kJ/m²

@Temperature 23.0 °C
52.3 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 122 µm/m-°C

@Temperature 23.0 - 60.0 °C
67.8 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
CTE, linear, Transverse to Flow 157 µm/m-°C

@Temperature 23.0 - 60.0 °C
87.2 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 53.0 °C
127 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
Electrical Properties Metric English Comments
Surface Resistance 100 - 10000 ohm
100 - 10000 ohm
ASTM D 257