SABIC Innovative Plastics LNP Faradex DX07304 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP FARADEX |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Faradex DX07304 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
CF filled grade with EMI shieldingThis data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ASTM D 792 |
| 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0017 cm/cm @Time 86400 sec |
0.0017 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0021 cm/cm @Time 86400 sec |
0.0021 in/in @Time 24.0 hour |
ASTM D 955 |
| Melt Flow | 11 g/10 min @Load 2.16 kg, Temperature 300 °C |
11 g/10 min @Load 4.76 lb, Temperature 572 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 133 MPa | 19300 psi | Type I, 5 mm/min; ASTM D 638 |
| Elongation at Break | 1.1 % | 1.1 % | Type I, 5 mm/min; ASTM D 638 |
| Tensile Modulus | 23.19 GPa | 3363 ksi | 50 mm/min; ASTM D 638 |
| 23.38 GPa | 3391 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 207 MPa | 30000 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Yield Strength | 210 MPa | 30500 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 19.6 GPa | 2840 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 0.370 J/cm @Temperature 23.0 °C |
0.693 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 2.96 J/cm @Temperature 23.0 °C |
5.55 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 15.0 kJ/m² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C | 162 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 72.0 °C @Thickness 3.20 mm |
162 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Flammability, UL94 | V-0 @Thickness 1.00 mm |
V-0 @Thickness 0.0394 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 7300 ohm-cm | 7300 ohm-cm | ASTM D 257 |
| 50000 ohm-cm | 50000 ohm-cm | IEC 60093 | |
| Surface Resistance | 10000 ohm | 10000 ohm | ROA; IEC 60093 |
| 438000 ohm | 438000 ohm | ASTM D 257 | |
| Shielding Effectiveness | 30 dB @Thickness 3.00 mm |
30 dB @Thickness 0.118 in |
SABIC Method |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® LUX9136C PC COPOLYMER (Asia Pacific)
- Lehmann & Voss LUVOCOM® 1105-7826/BL PEEK, with glass fiber
- Indium Corp. InCl3 Indium Trichloride
- Schott Glass 8245 Borosilicate Glass
- Plenco 7476 Phenolic, Granular, Transfer Molded
- Loctite® 420 General Purpose Ethyl Cyanoacrylate Bonding Adhesive
- Cotronics 4700 Ultra Temp Adhesive and Casting Epoxy, General Purpose
- Ascend Performance Materials Vydyne® R543H BK02 Nylon 66, 43% Glass Reinforced, Conditioned
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 20 PHR N330 (HAF) Filler
- XXXPC Phenolic Laminate
Copyright © lookpolymers.com All Rights Reserved