SABIC Innovative Plastics LNP FARADEX DX11003 PC (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP FARADEX
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP FARADEX DX11003 PC (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP FARADEX DX11003 is a compound based on Polycarbonate resin potentially suitable to meet high frequency electromagnetic absorption requirments. The compound is also an excellent candidate for many ESD applications.
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
ASTM D792
Water Absorption 0.25 %

@Time 86400 sec
0.25 %

@Time 24.0 hour
ISO 62-1
Moisture Absorption 0.140 %
0.140 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0080 cm/cm

@Time 86400 sec
0.0080 in/in

@Time 24.0 hour
ASTM D955
0.0084 cm/cm

@Time 86400 sec
0.0084 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0080 cm/cm

@Time 86400 sec
0.0080 in/in

@Time 24.0 hour
ASTM D955
0.0082 cm/cm

@Time 86400 sec
0.0082 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 53.0 MPa
7690 psi
5 mm/min; ISO 527
56.0 MPa
8120 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 60.0 MPa
8700 psi
5 mm/min; ISO 527
62.0 MPa
8990 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 8.8 %
8.8 %
5 mm/min; ISO 527
9.5 %
9.5 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 4.4 %
4.4 %
5 mm/min; ISO 527
4.9 %
4.9 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 2.68 GPa
389 ksi
50 mm/min; ASTM D638
2.90 GPa
421 ksi
1 mm/min; ISO 527
Flexural Strength 102 MPa
14800 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Yield Strength 102 MPa
14800 psi
2 mm/min; ISO 178
Flexural Modulus 2.89 GPa
419 ksi
1.3 mm/min, 50 mm span; ASTM D790
3.10 GPa
450 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.640 J/cm
1.20 ft-lb/in
ASTM D256
Izod Impact, Unnotched 12.17 J/cm
22.80 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 98.0 kJ/m²
46.6 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 8.00 J
5.90 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 138 °C

@Thickness 3.20 mm
280 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 127 °C
261 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
127 °C

@Thickness 3.20 mm
261 °F

@Thickness 0.126 in
unannealed; ASTM D648
Electrical Properties Metric English Comments
Surface Resistance 100 - 1.00e+6 ohm
100 - 1.00e+6 ohm
ASTM D257