SABIC Innovative Plastics LNP FARADEX AS003 ABS (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP FARADEX
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP FARADEX AS003 ABS (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Faradex* AS003 is a compound based on Acrylonitrile Butadiene Styrene resin containing Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding.
Physical Properties Metric English Comments
Density 1.15 g/cc
0.0415 lb/in³
ISO 1183
1.16 g/cc
0.0419 lb/in³
ASTM D792
Moisture Absorption 0.200 %
0.200 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0027 cm/cm

@Time 86400 sec
0.0027 in/in

@Time 24.0 hour
ISO 294
0.0030 cm/cm

@Time 86400 sec
0.0030 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0039 cm/cm

@Time 86400 sec
0.0039 in/in

@Time 24.0 hour
ISO 294
0.0040 cm/cm

@Time 86400 sec
0.0040 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 37.0 MPa
5370 psi
ISO 527
39.0 MPa
5660 psi
ASTM D638
Tensile Strength, Yield 38.0 MPa
5510 psi
ISO 527
42.0 MPa
6090 psi
ASTM D638
Elongation at Break 2.8 %
2.8 %
ISO 527
6.2 %
6.2 %
ASTM D638
Elongation at Yield 2.2 %
2.2 %
ISO 527
2.6 %
2.6 %
ASTM D638
Tensile Modulus 2.70 GPa
392 ksi
1 mm/min; ISO 527
3.15 GPa
457 ksi
50 mm/min; ASTM D638
Flexural Strength 66.0 MPa
9570 psi
ISO 178
75.0 MPa
10900 psi
ASTM D790
Flexural Modulus 2.80 GPa
406 ksi
ISO 178
3.04 GPa
441 ksi
ASTM D790
Izod Impact, Notched 0.530 J/cm
0.993 ft-lb/in
ASTM D256
Izod Impact, Unnotched 3.07 J/cm
5.75 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 18.0 kJ/m²
8.57 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 15.0 J
11.1 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 71.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
39.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
77.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
43.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 63.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
35.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
93.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
51.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 93.0 °C
199 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
96.0 °C

@Thickness 3.20 mm
205 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 78.0 °C
172 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
88.0 °C

@Thickness 3.20 mm
190 °F

@Thickness 0.126 in
unannealed; ASTM D648
Electrical Properties Metric English Comments
Volume Resistivity 10000 ohm-cm
10000 ohm-cm
ASTM D257
Surface Resistance 10 - 1000 ohm
10 - 1000 ohm
ASTM D257
Shielding Effectiveness 50 - 65 dB

@Thickness 3.00 mm
50 - 65 dB

@Thickness 0.118 in
SABIC Method