SABIC Innovative Plastics LNP Colorcomp D10009 PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Colorcomp
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Colorcomp D10009 PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Colorcomp* D10009 is a compound based on Polycarbonate resin containing Flame Retardant, Unfilled Custom Color. Added features of this material include: Flame Retardant.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.21 g/cc
0.0437 lb/in³
ASTM D 792
1.21 g/cc
0.0437 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.10 %

@Time 86400 sec
0.10 %

@Time 24.0 hour
50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0078 cm/cm

@Time 86400 sec
0.0078 in/in

@Time 24.0 hour
ISO 294
0.0070 - 0.0090 cm/cm

@Time 86400 sec
0.0070 - 0.0090 in/in

@Time 24.0 hour
ASTM D 955
Linear Mold Shrinkage, Transverse 0.0070 - 0.0090 cm/cm

@Time 86400 sec
0.0070 - 0.0090 in/in

@Time 24.0 hour
ASTM D 955
0.0083 cm/cm

@Time 86400 sec
0.0083 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 48.0 MPa
6960 psi
ASTM D 638
51.0 MPa
7400 psi
ISO 527
Tensile Strength, Yield 58.0 MPa
8410 psi
ASTM D 638
58.0 MPa
8410 psi
ISO 527
Elongation at Break 48.5 %
48.5 %
ASTM D 638
90.6 %
90.6 %
ISO 527
Elongation at Yield 5.7 %
5.7 %
ISO 527
5.8 %
5.8 %
ASTM D 638
Tensile Modulus 2.06 GPa
299 ksi
50 mm/min; ASTM D 638
2.16 GPa
313 ksi
1 mm/min; ISO 527
Flexural Strength 73.0 MPa
10600 psi
ISO 178
Flexural Modulus 2.06 GPa
299 ksi
ASTM D 790
2.10 GPa
305 ksi
ISO 178
Izod Impact, Notched 1.54 J/cm

@Temperature 23.0 °C
2.89 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 21.14 J/cm

@Temperature 23.0 °C
39.60 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 15.0 kJ/m²

@Temperature 23.0 °C
7.14 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 191 kJ/m²

@Temperature 23.0 °C
90.9 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
Impact Test 37.0 J
27.3 ft-lb
Multiaxial Impact; ISO 6603
54.0 J

@Temperature 23.0 °C
39.8 ft-lb

@Temperature 73.4 °F
Instrumented Impact Energy @ peak; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
70.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
39.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
40.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
40.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 136 °C
277 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
137 °C

@Thickness 3.20 mm
279 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 120 °C
248 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
126 °C

@Thickness 3.20 mm
259 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL 94 by SABIC-IP