SABIC Innovative Plastics LNP COLORCOMP W10009I PBT (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Colorcomp |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP COLORCOMP W10009I PBT (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* W10009I is a compound based on Polybutylene Terephalate resin containing Flame Retardant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.023 cm/cm | 0.023 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 42.0 MPa | 6090 psi | 5 mm/min; ISO 527 |
| Elongation at Yield | 4.2 % | 4.2 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 1.90 GPa | 276 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 68.0 MPa | 9860 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.90 GPa | 276 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 125 kJ/m² | 59.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 201 °C | 394 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
UL 94 by SABIC-IP |