SABIC Innovative Plastics LNP COLORCOMP J1000R PES (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyethersulfone (PES)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Colorcomp
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP COLORCOMP J1000R PES (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* COLORCOMP* J1000R is a compound based on Polyethersulfone resin. Added features include : Mold Release
Physical Properties Metric English Comments
Density 1.37 g/cc
0.0495 lb/in³
ISO 1183
Water Absorption 0.90 %

@Time 86400 sec
0.90 %

@Time 24.0 hour
ISO 62-1
Linear Mold Shrinkage, Flow 0.0090 cm/cm
0.0090 in/in
SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 71.0 MPa
10300 psi
50 mm/min; ISO 527
Tensile Strength, Yield 89.0 MPa
12900 psi
50 mm/min; ISO 527
Elongation at Yield 6.7 %
6.7 %
50 mm/min; ISO 527
Tensile Modulus 2.70 GPa
392 ksi
1 mm/min; ISO 527
Flexural Yield Strength 128 MPa
18600 psi
2 mm/min; ISO 178
Flexural Modulus 2.70 GPa
392 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 59.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
32.8 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
CTE, linear, Transverse to Flow 58.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
32.2 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 199 °C
390 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af