SABIC Innovative Plastics LNP COLORCOMP D1000P PC (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Colorcomp
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP COLORCOMP D1000P PC (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Colorcomp* D1000P is a compound based on Polycarbonate resin containing Unfilled Custom Color. Added features of this material include: Exceptional Processing.
Physical Properties Metric English Comments
Density 1.19 g/cc
0.0430 lb/in³
ISO 1183
1.20 g/cc
0.0434 lb/in³
ASTM D792
Linear Mold Shrinkage, Flow 0.0065 cm/cm

@Time 86400 sec
0.0065 in/in

@Time 24.0 hour
ISO 294
0.0060 - 0.0080 cm/cm

@Time 86400 sec
0.0060 - 0.0080 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0075 cm/cm

@Time 86400 sec
0.0075 in/in

@Time 24.0 hour
ISO 294
0.0070 - 0.0090 cm/cm

@Time 86400 sec
0.0070 - 0.0090 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 56.0 MPa
8120 psi
ASTM D638
59.0 MPa
8560 psi
ISO 527
Tensile Strength, Yield 62.0 MPa
8990 psi
ASTM D638
64.0 MPa
9280 psi
ISO 527
Elongation at Break 78.7 %
78.7 %
ASTM D638
87 %
87 %
ISO 527
Elongation at Yield 5.3 %
5.3 %
ASTM D638
5.6 %
5.6 %
ISO 527
Tensile Modulus 2.06 GPa
299 ksi
50 mm/min; ASTM D638
2.21 GPa
321 ksi
1 mm/min; ISO 527
Flexural Strength 81.0 MPa
11700 psi
ISO 178
Flexural Modulus 2.30 GPa
334 ksi
ISO 178
2.75 GPa
399 ksi
ASTM D790
Izod Impact, Notched 5.44 J/cm
10.2 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 13.0 kJ/m²
6.19 ft-lb/in²
80*10*4; ISO 180/1A
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 124 °C
255 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
123 °C

@Thickness 3.20 mm
253 °F

@Thickness 0.126 in
unannealed; ASTM D648