SABIC Innovative Plastics LNP COLORCOMP D10006U PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Colorcomp |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP COLORCOMP D10006U PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* COLORCOMP* D10006U is an unfilled Polycarbonate. Added features include: Lasermarking Capability, UL Listed.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Density | 1.24 g/cc | 0.0448 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.130 % | 0.130 % | 50% RH, 24 hrs; ASTM D570 |
| 0.240 % | 0.240 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.010 cm/cm @Time 86400 sec |
0.0080 - 0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 54.0 MPa | 7830 psi | Type I, 5 mm/min; ASTM D638 |
| 55.0 MPa | 7980 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 5 mm/min; ISO 527 |
| 61.0 MPa | 8850 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 79 % | 79 % | Type I, 5 mm/min; ASTM D638 |
| 151 % | 151 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 6.0 % | 6.0 % | Type I, 5 mm/min; ASTM D638 |
| 6.0 % | 6.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 2.46 GPa | 357 ksi | 1 mm/min; ISO 527 |
| 2.47 GPa | 358 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 89.0 MPa | 12900 psi | ISO 178 |
| Flexural Modulus | 2.32 GPa | 336 ksi | 2 mm/min; ISO 178 |
| 2.44 GPa | 354 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 7.41 J/cm | 13.9 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 58.0 kJ/m² | 27.6 ft-lb/in² | 80*10*4; ISO 180/1A |
| Dart Drop, Total Energy | 63.0 J @Temperature 23.0 °C |
46.5 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 76.0 J | 56.1 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 71.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
39.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 69.3 µm/m-°C @Temperature -30.0 - 30.0 °C |
38.5 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 136 °C | 277 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 125 °C @Thickness 3.20 mm |
257 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 |
Users viewing this material also viewed the following:
- RheTech Products FT7016-01UV Thermoplastic Polyolefin, UV Stabilized, Black
- Polymax® Maxelast® P3755 TPE, PP Overmold or Standalone use
- SABIC Innovative Plastics Cycoloy® CY9650 PC+ABS (Asia Pacific)
- SABIC Innovative Plastics Lexan® HPM1914 PC Copolymer (Europe-Africa-Middle East)
- SABIC Innovative Plastics Lexan® HPXS8R PC Copolymer
- Total PPH 3862 Homopolymer Polypropylene, Fiber Grade
- Overview of materials for Linear Low Density Polyethylene (LLDPE), Extrusion Grade
- G-2706 Styrene-based Biomedical Elastomer
- Lucite International Diakon® MG102 Acrylic Bead Polymer, High Transparency
- E-Polymers TEKAMID® JN1 PPE+PA66 Un-reinforced High flow Heat resistance PA/PPE Alloy
Copyright © lookpolymers.com All Rights Reserved