- SABIC Innovative Plastics Geloy XTPMFR15 ASA+PC (Europe-Africa-Middle East)
SABIC Innovative Plastics Geloy XTPMFR15 ASA+PC (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , ASA Polymer , Polycarbonate (PC) , Polycarbonate/ASA Alloy, Unreinforced |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | GELOY |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Geloy XTPMFR15 ASA+PC (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Geloy XTPMFR15 is a chlorine and bromine free flame retardant ASA/PC blend with improved impact performance/ductility and an UL94 rating of V0 at 1.5mm. This grade has a f1 rating according UL746C.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Viscosity | 138000 cP @Temperature 260 °C |
138000 cP @Temperature 500 °F |
melt; 1500 sec-1; ISO 11443 |
| Melt Flow | 18 g/10 min @Load 2.16 kg, Temperature 260 °C |
18 g/10 min @Load 4.76 lb, Temperature 500 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 27 g/10 min @Load 10.0 kg, Temperature 220 °C |
27 g/10 min @Load 22.0 lb, Temperature 428 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 | |
| 30 g/10 min @Load 10.0 kg, Temperature 220 °C |
30 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | 50 mm/min; ISO 527 |
| 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D 638 | |
| 48.0 MPa | 6960 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 56.0 MPa | 8120 psi | 50 mm/min; ISO 527 |
| 57.0 MPa | 8270 psi | Type I, 5 mm/min; ASTM D 638 | |
| 61.0 MPa | 8850 psi | Type I, 50 mm/min; ASTM D 638 | |
| Elongation at Break | 55 % | 55 % | Type I, 50 mm/min; ASTM D 638 |
| 60 % | 60 % | 50 mm/min; ISO 527 | |
| 62 % | 62 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 4.0 % | 4.0 % | Type I, 50 mm/min; ASTM D 638 |
| 4.0 % | 4.0 % | Type I, 5 mm/min; ASTM D 638 | |
| 4.0 % | 4.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.25 GPa | 326 ksi | 1 mm/min; ISO 527 |
| 2.50 GPa | 363 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Yield Strength | 88.0 MPa | 12800 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched | 1.18 J/cm @Temperature -30.0 °C |
2.21 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 |
| 7.00 J/cm @Temperature 23.0 °C |
13.1 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A |
| 26.0 kJ/m² @Temperature 0.000 °C |
12.4 ft-lb/in² @Temperature 32.0 °F |
80*10*4; ISO 180/1A | |
| 50.0 kJ/m² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 5.80 J/cm² @Temperature 23.0 °C |
27.6 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 68.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 99.0 °C | 210 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Vicat Softening Point | 103 °C | 217 °F | Rate B/50; ISO 306 |
| 104 °C | 219 °F | Rate B/120; ISO 306 | |
| 111 °C | 232 °F | Rate A/50; ISO 306 | |
| Flammability, UL94 | V-1 @Thickness 1.20 mm |
V-1 @Thickness 0.0472 in |
UL 94 |
| V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 | |
| 5VB @Thickness 2.00 mm |
5VB @Thickness 0.0787 in |
UL 94 | |
| 5VA @Thickness 3.00 mm |
5VA @Thickness 0.118 in |
UL 94 | |
| Oxygen Index | 30 % | 30 % | LOI; ISO 4589 |
| Glow Wire Test | 800 °C @Thickness 2.00 mm |
1470 °F @Thickness 0.0787 in |
Glow Wire Ignitability Temperature; IEC 60695-2-13 |
| 800 °C @Thickness 3.00 mm |
1470 °F @Thickness 0.118 in |
Glow Wire Ignitability Temperature; IEC 60695-2-13 | |
| 825 °C @Thickness 1.00 mm |
1520 °F @Thickness 0.0394 in |
Glow Wire Ignitability Temperature; IEC 60695-2-13 | |
| 850 °C @Thickness 0.800 mm |
1560 °F @Thickness 0.0315 in |
Glow Wire Ignitability Temperature; IEC 60695-2-13 | |
| 960 °C @Thickness 0.800 mm |
1760 °F @Thickness 0.0315 in |
Glow Wire Flammability Index; IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | PLC code 0; UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | surface, PLC code 0; UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| UV-light, water exposure/immersion | F1 | UL 746C |