SABIC Innovative Plastics Geloy FXW751SK ASA+PC (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , ASA Polymer , Polycarbonate (PC) , Polycarbonate/ASA Alloy, Unreinforced
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name GELOY
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Geloy FXW751SK ASA+PC (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Sparkle Metallic VisualFx ASA+PC Resin - Weatherable, High Heat & Impact ResinThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Specific Gravity 1.16 g/cc
1.16 g/cc
ASTM D 792
Density 1.16 g/cc
0.0419 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.25 %
0.25 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 1.0 %

@Temperature 23.0 °C
 1.0 %

@Temperature 73.4 °F
 ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 7.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 7.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
8.3 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 8.3 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 48.0 MPa
6960 psi
Type I, 50 mm/min; ASTM D 638
48.0 MPa
6960 psi
50 mm/min; ISO 527
Tensile Strength, Yield 60.0 MPa
8700 psi
50 mm/min; ISO 527
62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break 49 %
49 %
Type I, 50 mm/min; ASTM D 638
77 %
77 %
50 mm/min; ISO 527
Elongation at Yield 4.2 %
4.2 %
Type I, 50 mm/min; ASTM D 638
4.2 %
4.2 %
50 mm/min; ISO 527
Tensile Modulus 2.68 GPa
389 ksi
5 mm/min; ASTM D 638
2.90 GPa
421 ksi
1 mm/min; ISO 527
Flexural Yield Strength 78.0 MPa
11300 psi
2 mm/min; ISO 178
95.0 MPa
13800 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.70 GPa
392 ksi
2 mm/min; ISO 178
2.75 GPa
399 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 0.0300 J/cm

@Temperature 23.0 °C
 0.0562 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature -30.0 °C
 2.38 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
17.0 kJ/m²

@Temperature 23.0 °C
 8.09 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 1.70 J/cm²

@Temperature 23.0 °C
 8.09 ft-lb/in²

@Temperature 73.4 °F
 V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 43.0 J

@Temperature 23.0 °C
 31.7 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 40.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 40.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 40.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 40.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C
199 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
89.0 °C

@Thickness 3.20 mm
 192 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Vicat Softening Point 105 °C
221 °F
Rate B/50; ASTM D 1525
108 °C
226 °F
Rate B/50; ISO 306
109 °C
228 °F
Rate B/120; ISO 306