SABIC Innovative Plastics GELOY HRA170D ASA+PC (Europe-Africa-Middle East)

Category	Polymer , Thermoplastic , ASA Polymer , Polycarbonate (PC) , Polycarbonate/ASA Alloy, Unreinforced
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	GELOY
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics GELOY HRA170D ASA+PC (Europe-Africa-Middle East).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

GELOY HRA170D resin is a PC-ASA blend with permanent antistatic behavior. It is typically used in applications that require antidust properties and high impact retention. Geloy HRA170D resin is typically used in various outdoor and indoor applications requiring superior heat aging properties and colour stability.

Physical Properties	Metric	English	Comments
Specific Gravity	1.16 g/cc	1.16 g/cc	ASTM D792
Density	1.16 g/cc	0.0419 lb/in³	ISO 1183
Melt Flow	8.0 g/10 min @Load 10.0 kg, Temperature 220 °C	8.0 g/10 min @Load 22.0 lb, Temperature 428 °F	ISO 1133
	8.5 g/10 min @Load 10.0 kg, Temperature 220 °C	8.5 g/10 min @Load 22.0 lb, Temperature 428 °F	ASTM D1238
	30 g/10 min @Load 5.00 kg, Temperature 260 °C	30 g/10 min @Load 11.0 lb, Temperature 500 °F	ASTM D1238
Melt Index of Compound	8.0 g/10 min @Load 10.0 kg, Temperature 220 °C	8.0 g/10 min @Load 22.0 lb, Temperature 428 °F	MVR [cm^3/10 min]; ISO 1133
	29 g/10 min @Load 5.00 kg, Temperature 260 °C	29 g/10 min @Load 11.0 lb, Temperature 500 °F	MVR [cm^3/10 min]; ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell L	57	57	ISO 2039-2
Hardness, H358/30	63.0 MPa	9140 psi	ISO 2039-1
Hardness, Shore D	77	77	ISO 868
Tensile Strength at Break	58.0 MPa	8410 psi	Type I, 5 mm/min; ASTM D638
	58.0 MPa	8410 psi	50 mm/min; ISO 527
	59.0 MPa	8560 psi	Type I, 50 mm/min; ASTM D638
	65.0 MPa	9430 psi	5 mm/min; ISO 527
Tensile Strength, Yield	50.0 MPa	7250 psi	Type I, 5 mm/min; ASTM D638
	51.0 MPa	7400 psi	5 mm/min; ISO 527
	54.0 MPa	7830 psi	50 mm/min; ISO 527
	54.0 MPa	7830 psi	Type I, 50 mm/min; ASTM D638
Elongation at Break	130 %	130 %	50 mm/min; ISO 527
	140 %	140 %	Type I, 50 mm/min; ASTM D638
	160 %	160 %	Type I, 5 mm/min; ASTM D638
Elongation at Yield	5.0 %	5.0 %	Type I, 50 mm/min; ASTM D638
	5.0 %	5.0 %	Type I, 5 mm/min; ASTM D638
	5.0 %	5.0 %	50 mm/min; ISO 527
	130 %	130 %	5 mm/min; ISO 527
Tensile Modulus	2.15 GPa	312 ksi	1 mm/min; ISO 527
	2.16 GPa	313 ksi	5 mm/min; ASTM D638
Flexural Yield Strength	80.0 MPa	11600 psi	2 mm/min; ISO 178
Flexural Modulus	2.10 GPa	305 ksi	2 mm/min; ISO 178
Izod Impact, Notched	7.50 J/cm	14.1 ft-lb/in	ASTM D256
	1.40 J/cm @Temperature -30.0 °C	2.62 ft-lb/in @Temperature -22.0 °F	ASTM D256
Izod Impact, Notched (ISO)	60.0 kJ/m²	28.6 ft-lb/in²	80104; ISO 180/1A
	125 kJ/m²	59.5 ft-lb/in²	80103; ISO 180/1A
	14.0 kJ/m² @Temperature -30.0 °C	6.66 ft-lb/in² @Temperature -22.0 °F	80104; ISO 180/1A
	17.0 kJ/m² @Temperature -30.0 °C	8.09 ft-lb/in² @Temperature -22.0 °F	80103; ISO 180/1A
Charpy Impact, Notched	12.8 J/cm²	60.9 ft-lb/in²	Edgew 80104 sp=62mm; ISO 179/1eA
	1.70 J/cm² @Temperature -30.0 °C	8.09 ft-lb/in² @Temperature -22.0 °F	Edgew 80104 sp=62mm; ISO 179/1eA

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	127 °C	261 °F	Flatw 80104 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi)	104 °C	219 °F	Flatw 80104 sp=64mm; ISO 75/Af
	106 °C @Thickness 3.20 mm	223 °F @Thickness 0.126 in	unannealed; ASTM D648
Vicat Softening Point	121 °C	250 °F	Rate B/50; ISO 306
	122 °C	252 °F	Rate B/120; ISO 306
	137 °C	279 °F	Rate A/50; ISO 306
	138 °C	280 °F	Rate A/120; ISO 306

Electrical Properties	Metric	English	Comments
Surface Resistance	1.00e+13 ohm	1.00e+13 ohm	ROA; IEC 60093