SABIC Innovative Plastics GELOY FXW750SK ASA+PC

Category Polymer , Thermoplastic , ASA Polymer , Polycarbonate (PC) , Polycarbonate/ASA Alloy, Unreinforced
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name GELOY
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics GELOY FXW750SK ASA+PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Sparkle Metallic VisualFx ASA+PC Resin - Med. Heat & Impact Resin
Physical Properties Metric English Comments
Specific Gravity 1.16 g/cc
1.16 g/cc
ASTM D792
Density 1.16 g/cc
0.0419 lb/in³
ISO 1183
Moisture Absorption 0.240 %
0.240 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.96 %
0.96 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 10.2 g/10 min

@Load 10.0 kg,
Temperature 220 °C
10.2 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ASTM D1238
Melt Index of Compound 8.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
8.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 44.0 MPa
6380 psi
50 mm/min; ISO 527
46.0 MPa
6670 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 57.0 MPa
8270 psi
50 mm/min; ISO 527
59.0 MPa
8560 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 31 %
31 %
Type I, 50 mm/min; ASTM D638
32 %
32 %
50 mm/min; ISO 527
Elongation at Yield 3.9 %
3.9 %
Type I, 50 mm/min; ASTM D638
3.9 %
3.9 %
50 mm/min; ISO 527
Tensile Modulus 2.70 GPa
392 ksi
5 mm/min; ASTM D638
3.01 GPa
437 ksi
1 mm/min; ISO 527
Flexural Yield Strength 85.0 MPa
12300 psi
2 mm/min; ISO 178
91.0 MPa
13200 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.60 GPa
377 ksi
2 mm/min; ISO 178
2.76 GPa
400 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
80*10*4; ISO 180/1A
3.00 kJ/m²

@Temperature -30.0 °C
1.43 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 0.900 J/cm²
4.28 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 7.00 J

@Temperature 23.0 °C
5.16 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
40.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
40.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
40.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
40.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C
185 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
85.0 °C

@Thickness 3.20 mm
185 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 101 °C
214 °F
Rate B/50; ASTM D1525
103 °C
217 °F
Rate B/50; ISO 306
104 °C
219 °F
Rate B/120; ISO 306