Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

SABIC Innovative Plastics GELOY FXW749SK ASA

Category Polymer , Thermoplastic , ASA Polymer
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name GELOY
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics GELOY FXW749SK ASA.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Sparkle VisualFx ASA Resin - Weatherable
Physical Properties Metric English Comments
Specific Gravity 1.11 g/cc
1.11 g/cc
ASTM D792
Density 1.11 g/cc
0.0401 lb/in³
ISO 1183
Moisture Absorption 0.200 %
0.200 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.80 %
0.80 %
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 9.2 g/10 min

@Load 10.0 kg,
Temperature 220 °C
9.2 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ASTM D1238
Melt Index of Compound 8.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
8.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 42.0 MPa
6090 psi
50 mm/min; ISO 527
45.0 MPa
6530 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 52.0 MPa
7540 psi
50 mm/min; ISO 527
54.0 MPa
7830 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 8.5 %
8.5 %
Type I, 50 mm/min; ASTM D638
14 %
14 %
50 mm/min; ISO 527
Elongation at Yield 2.7 %
2.7 %
50 mm/min; ISO 527
2.9 %
2.9 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.87 GPa
416 ksi
5 mm/min; ASTM D638
3.06 GPa
444 ksi
1 mm/min; ISO 527
Flexural Yield Strength 77.0 MPa
11200 psi
2 mm/min; ISO 178
85.0 MPa
12300 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.79 GPa
405 ksi
2 mm/min; ISO 178
2.93 GPa
425 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.580 J/cm
1.09 ft-lb/in
ASTM D256
0.210 J/cm

@Temperature -30.0 °C
0.393 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
2.00 kJ/m²

@Temperature -30.0 °C
0.952 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 3.00 J

@Temperature 23.0 °C
2.21 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
50.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
93.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
51.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 102 µm/m-°C

@Temperature -40.0 - 40.0 °C
56.7 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
104 µm/m-°C

@Temperature -40.0 - 40.0 °C
57.8 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 82.0 °C
180 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
81.0 °C

@Thickness 3.20 mm
178 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 95.0 °C
203 °F
Rate B/50; ASTM D1525
97.0 °C
207 °F
Rate B/50; ISO 306
99.0 °C
210 °F
Rate B/120; ISO 306