SABIC Innovative Plastics FL405 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics FL405 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Various weight reductions at 0.250"" (6.38 mm) wall. Impact resistant, superior processing, excellent surface. UL94 V-0 at 0.120
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | foam molded; ASTM D792 |
| 1.20 g/cc | 1.20 g/cc | ASTM D792 | |
| Water Absorption | 0.14 % @Time 86400 sec |
0.14 % @Time 24.0 hour |
ASTM D570 |
| Moisture Absorption at Equilibrium | 0.31 % | 0.31 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm @Thickness 6.40 mm |
0.0060 - 0.0080 in/in @Thickness 0.252 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 54.0 MPa @Thickness 6.35 mm |
7830 psi @Thickness 0.250 in |
ASTM D638 |
| Elongation at Break | 7.2 % @Thickness 6.35 mm |
7.2 % @Thickness 0.250 in |
ASTM D638 |
| Tensile Modulus | 2.10 GPa @Thickness 6.40 mm |
305 ksi @Thickness 0.252 in |
ASTM D638 |
| Flexural Yield Strength | 86.0 MPa | 12500 psi | 6.4 mm; ASTM D790 |
| Flexural Modulus | 2.48 GPa | 360 ksi | 6.4 mm; ASTM D790 |
| Izod Impact, Unnotched | 26.7 J/cm | 50.0 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 61.0 J | 45.0 ft-lb | SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 66.6 µm/m-°C @Temperature -40.0 - 95.0 °C |
37.0 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| Specific Heat Capacity | 1.34 J/g-°C | 0.320 BTU/lb-°F | ASTM C351 |
| Deflection Temperature at 0.46 MPa (66 psi) | 137 °C @Thickness 6.40 mm |
279 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C @Thickness 6.40 mm |
259 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| UL RTI, Electrical | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical with Impact | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical without Impact | 80.0 °C | 176 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 3.05 mm |
V-0 @Thickness 0.120 in |
UL 94 |
| 5VA @Thickness 6.10 mm |
5VA @Thickness 0.240 in |
UL 94 | |
| Oxygen Index | 39 % | 39 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 3.50e+17 ohm-cm | 3.50e+17 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.10e+17 ohm | >= 1.10e+17 ohm | ASTM D257 |
| Dielectric Constant | 2.42 @Frequency 100 Hz |
2.42 @Frequency 100 Hz |
ASTM D150 |
| 2.43 @Frequency 1.00e+6 Hz |
2.43 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Dissipation Factor | 0.0011 @Frequency 100 Hz |
0.0011 @Frequency 100 Hz |
ASTM D150 |
| 0.0044 @Frequency 1.00e+6 Hz |
0.0044 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| FOAM - ELECTRICAL 6.4 mm Wt Reduction | 20% | |
| FOAM - Flame Class Minimum Density | 1.06g/cm^3 | |
| FOAM - IMPACT 6.4 mm Wt Reduction | 10% | |
| FOAM - MECHANICAL 6.4 mm Wt Reduction | 10% | |
| FOAM - PHYSICAL 6.4mm Wt Reduction | 10% | |
| FOAM - THERMAL 6.4mm Wt Reduction | 10% | |
| Radiant Panel Listing | YES | UL Tested |