- SABIC Innovative Plastics Extem UH1016M TPI Blend (Europe-Africa-Middle East)
SABIC Innovative Plastics Extem UH1016M TPI Blend (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyimide, Thermoplastic |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Extem |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Extem UH1016M TPI Blend (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High heat amorphous TPI Blend, Chemical ResistantThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.37 g/cc | 1.37 g/cc | ASTM D 792 |
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 |
| Water Absorption | 0.60 % @Temperature 23.0 °C, Time 173000 sec |
0.60 % @Temperature 73.4 °F, Time 48.0 hour |
ASTM D 570 |
| Moisture Absorption at Equilibrium | 0.00 % | 0.00 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.00 % @Temperature 23.0 °C |
0.00 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.010 cm/cm @Thickness 3.20 mm |
0.0080 - 0.010 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 12 g/10 min @Load 6.60 kg, Temperature 400 °C |
12 g/10 min @Load 14.6 lb, Temperature 752 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 105 MPa | 15200 psi | 5 mm/min; ISO 527 |
| 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 112 MPa | 16200 psi | 5 mm/min; ISO 527 |
| 120 MPa | 17400 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 10 % | 10 % | Type I, 5 mm/min; ASTM D 638 |
| 17 % | 17 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 9.0 % | 9.0 % | Type I, 5 mm/min; ASTM D 638 |
| 9.0 % | 9.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 3.50 GPa | 508 ksi | 1 mm/min; ISO 527 |
| 3.80 GPa | 551 ksi | 5 mm/min; ASTM D 638 | |
| Flexural Yield Strength | 155 MPa | 22500 psi | 2 mm/min; ISO 178 |
| 175 MPa | 25400 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 3.00 GPa | 435 ksi | 2 mm/min; ISO 178 |
| 3.52 GPa | 511 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.600 J/cm @Temperature 23.0 °C |
1.12 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Charpy Impact, Notched | 1.80 J/cm² @Temperature 23.0 °C |
8.57 ft-lb/in² @Temperature 73.4 °F |
ISO 179/2C |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 46.0 µm/m-°C @Temperature 23.0 - 150 °C |
25.6 µin/in-°F @Temperature 73.4 - 302 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 47.0 µm/m-°C @Temperature 23.0 - 150 °C |
26.1 µin/in-°F @Temperature 73.4 - 302 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 263 °C @Thickness 3.20 mm |
505 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 236 °C | 457 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 240 °C @Thickness 3.20 mm |
464 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 257 °C | 495 °F | Rate B/50; ASTM D 1525 |
| 261 °C | 502 °F | Rate B/50; ISO 306 | |
| 262 °C | 504 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- Resin Technology Group UV-406 High Clarity, Moisture Resistant, UV Curing Bonder
- SABIC 318CN Linear Low Density Polyethylene for Wire & Cable
- Eastman E6838-902F Polyethylene Film (discontinued **)
- Ineos K54-05 HDPE
- SABIC Innovative Plastics LNP LUBRICOMP RAL22I PA 66
- SABIC Innovative Plastics ULTEM 1010R PEI (Asia Pacific)
- A. Schulman POLYFORT™ FPP 1237 CaCO3 filled homopolymer polypropylene
- Bostik 6332 Quick Setup EVA Glue Stick
- Loctite® 620 High Temperature Retaining Compound
- LATI Latimass 82-05 D040 PA12
Copyright © lookpolymers.com All Rights Reserved