SABIC Innovative Plastics EXTEM VH1003P PEI Copolymer (Asia Pacific)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Extem
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics EXTEM VH1003P PEI Copolymer (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Transparent, Thermoplastic Polyimide (TPI) resin with a glass transition temperature (Tg) of 247C. Powder version of VH1003. This resin is a Dual-use item and is subject to export control restrictions under both U.S. 15 CFR 774 and Annex I of Reg. (EC) 428/2009 as ECCN 1C008. Diversion contrary to law is prohibited.
Physical Properties Metric English Comments
Specific Gravity 1.30 g/cc
1.30 g/cc
ASTM D792
Density 1.30 g/cc
0.0470 lb/in³
ISO 1183
Moisture Absorption 0.600 %
0.600 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 1.75 %
1.75 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
on Tensile Bar; SABIC Method
0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 15.5 g/10 min

@Load 6.60 kg,
Temperature 367 °C
15.5 g/10 min

@Load 14.6 lb,
Temperature 693 °F
ASTM D1238
Melt Index of Compound 8.0 g/10 min

@Load 5.00 kg,
Temperature 360 °C
8.0 g/10 min

@Load 11.0 lb,
Temperature 680 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, H358/30 140 MPa
20300 psi
ISO 2039-1
Tensile Strength at Break 78.0 MPa
11300 psi
5 mm/min; ISO 527
96.0 MPa
13900 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 95.0 MPa
13800 psi
5 mm/min; ISO 527
96.0 MPa
13900 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 50 %
50 %
Type I, 5 mm/min; ASTM D638
50 %
50 %
5 mm/min; ISO 527
Elongation at Yield 6.0 %
6.0 %
Type I, 5 mm/min; ASTM D638
8.5 %
8.5 %
5 mm/min; ISO 527
Tensile Modulus 3.11 GPa
451 ksi
1 mm/min; ISO 527
3.51 GPa
509 ksi
5 mm/min; ASTM D638
Flexural Strength 159 MPa
23100 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Yield Strength 123 MPa
17800 psi
2 mm/min; ISO 178
155 MPa
22500 psi
2.6 mm/min, 100 mm span; ASTM D790
Flexural Modulus 3.08 GPa
447 ksi
2 mm/min; ISO 178
3.17 GPa
460 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.690 J/cm
1.29 ft-lb/in
ASTM D256
0.740 J/cm

@Temperature -30.0 °C
1.39 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D4812
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4; ISO 180/1A
5.00 kJ/m²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*4; ISO 180/1U
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
80*10*4; ISO 180/1U
Charpy Impact Unnotched NB
NB
Edgew 80*10*4 sp=62mm; ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eU
Dart Drop, Total Energy 33.0 J

@Temperature 23.0 °C
24.3 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 50.0 µm/m-°C

@Temperature -40.0 - 150 °C
27.8 µin/in-°F

@Temperature -40.0 - 302 °F
ASTM E 831
50.0 µm/m-°C

@Temperature 23.0 - 150 °C
27.8 µin/in-°F

@Temperature 73.4 - 302 °F
ISO 11359-2
CTE, linear, Transverse to Flow 50.0 µm/m-°C

@Temperature -40.0 - 150 °C
27.8 µin/in-°F

@Temperature -40.0 - 302 °F
ASTM E 831
50.0 µm/m-°C

@Temperature 23.0 - 150 °C
27.8 µin/in-°F

@Temperature 73.4 - 302 °F
ISO 11359-2
Thermal Conductivity 0.220 W/m-K
1.53 BTU-in/hr-ft²-°F
ASTM E 1530
Deflection Temperature at 0.46 MPa (66 psi) 237 °C

@Thickness 6.40 mm
459 °F

@Thickness 0.252 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 228 °C
442 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
217 °C

@Thickness 3.20 mm
423 °F

@Thickness 0.126 in
unannealed; ASTM D648
230 °C

@Thickness 6.40 mm
446 °F

@Thickness 0.252 in
unannealed; ASTM D648
Vicat Softening Point 238 °C
460 °F
Rate B/120; ISO 306
242 °C
468 °F
Rate B/50; ASTM D1525
242 °C
468 °F
Rate B/50; ISO 306
Glass Transition Temp, Tg 247 °C
477 °F
Oxygen Index 45 %
45 %
ISO 4589
Glow Wire Test 850 °C
1560 °F
IEC 60695-2-13
960 °C

@Thickness 3.20 mm
1760 °F

@Thickness 0.126 in
IEC 60695-2-12
Optical Properties Metric English Comments
Haze 2.0 %

@Thickness 2.54 mm
2.0 %

@Thickness 0.100 in
ASTM D1003
Transmission, Visible 58 %
58 %
2.54 mm; ASTM D1003
Electrical Properties Metric English Comments
Dielectric Constant 3.41

@Frequency 100 Hz
3.41

@Frequency 100 Hz
ASTM D150
3.41

@Frequency 1000 Hz
3.41

@Frequency 1000 Hz
ASTM D150
Dielectric Strength 17.0 kV/mm

@Thickness 3.20 mm
432 kV/in

@Thickness 0.126 in
in oil; ASTM D149
Dissipation Factor 0.0010

@Frequency 1000 Hz
0.0010

@Frequency 1000 Hz
IEC 60250
0.0070

@Frequency 1.00e+6 Hz
0.0070

@Frequency 1.00e+6 Hz
IEC 60250
0.0080

@Frequency 100 Hz
0.0080

@Frequency 100 Hz
IEC 60250
0.025

@Frequency 50.0 - 60.0 Hz
0.025

@Frequency 50.0 - 60.0 Hz
IEC 60250
Comparative Tracking Index 175 V
175 V
IEC 60112
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C Passes
IEC 60695-10-2