SABIC Innovative Plastics Cycoloy® LG9000 PC+ABS (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® LG9000 PC+ABS (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
CYCOLOY LG9000 is a low gloss PC+ABS injection moulding grade. LG9000 combines good impact / heat and UV resistance with a low gloss surface appearence. It is suitable for automotive interior applications.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.60 %

@Temperature 23.0 °C
0.60 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
on tensile bar; SABIC Method
Melt Flow 20 g/10 min

@Load 5.00 kg,
Temperature 260 °C
20 g/10 min

@Load 11.0 lb,
Temperature 500 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 116
116
ISO 2039-2
Hardness, H358/30 93.0 MPa
13500 psi
ISO 2039-1
Tensile Strength at Break 40.0 MPa
5800 psi
5 mm/min; ISO 527
45.0 MPa
6530 psi
50 mm/min; ISO 527
Tensile Strength, Yield 50.0 MPa
7250 psi
5 mm/min; ISO 527
50.0 MPa
7250 psi
50 mm/min; ISO 527
Elongation at Break 10 %
10 %
5 mm/min; ISO 527
10 %
10 %
50 mm/min; ISO 527
Elongation at Yield 4.0 %
4.0 %
5 mm/min; ISO 527
4.0 %
4.0 %
50 mm/min; ISO 527
Tensile Modulus 2.30 GPa
334 ksi
1 mm/min; ISO 527
Flexural Yield Strength 81.0 MPa
11700 psi
2 mm/min; ISO 178
Flexural Modulus 2.40 GPa
348 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 15.0 kJ/m²

@Temperature -30.0 °C
7.14 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
35.0 kJ/m²

@Temperature 23.0 °C
16.7 ft-lb/in²

@Temperature 73.4 °F
80*10*3; ISO 180/1A
Charpy Impact, Notched 1.50 J/cm²

@Temperature -30.0 °C
7.14 ft-lb/in²

@Temperature -22.0 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
3.50 J/cm²

@Temperature 23.0 °C
16.7 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
Taber Abrasion, mg/1000 Cycles 82

@Load 1.00 kg
82

@Load 2.20 lb
CS-17; SABIC Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
44.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
44.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Thermal Conductivity 0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
ISO 8302
Hot Ball Pressure Test <= 110 °C
<= 230 °F
IEC 60695-10-2
Deflection Temperature at 0.46 MPa (66 psi) 120 °C
248 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 97.0 °C
207 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
Vicat Softening Point 122 °C
252 °F
Rate B/50; ISO 306
124 °C
255 °F
Rate B/120; ISO 306
UL RTI, Electrical 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical with Impact 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical without Impact 60.0 °C
140 °F
UL 746B
Flammability, UL94 HB

@Thickness 1.00 mm
HB

@Thickness 0.0394 in
UL 94
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
2nd value; UL 94
Flame Spread 35.0 mm/min

@Thickness 1.00 mm
1.38 in/min

@Thickness 0.0394 in
FMVSS 302
Glow Wire Test 650 °C

@Thickness 3.20 mm
1200 °F

@Thickness 0.126 in
Glow Wire Flammability Index; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 2.6

@Frequency 1.00e+6 Hz
2.6

@Frequency 1.00e+6 Hz
IEC 60250
2.6

@Frequency 50.0 - 60.0 Hz
2.6

@Frequency 50.0 - 60.0 Hz
IEC 60250
Dielectric Strength 17.0 kV/mm

@Thickness 3.20 mm
432 kV/in

@Thickness 0.126 in
in oil; IEC 60243-1
25.0 kV/mm

@Thickness 1.60 mm
635 kV/in

@Thickness 0.0630 in
in oil; IEC 60243-1
35.0 kV/mm

@Thickness 0.800 mm
889 kV/in

@Thickness 0.0315 in
in oil; IEC 60243-1
Dissipation Factor 0.0010

@Frequency 50.0 - 60.0 Hz
0.0010

@Frequency 50.0 - 60.0 Hz
IEC 60250
0.0090

@Frequency 1.00e+6 Hz
0.0090

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 275 V
275 V
IEC 60112
250 - 400 V
250 - 400 V
PLC code 2; UL 746A
Hot Wire Ignition, HWI 30 - 60 sec
30 - 60 sec
PLC code 2; UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
surface, PLC code 0; UL 746A
Descriptive Properties Value Comments
Ball Pressure Test, 75°C +/- 2°C PASSES
IEC 60695-10-2