SABIC Innovative Plastics Cycoloy® FXC630ME PC+ABS

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® FXC630ME PC+ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Color package may affect performance. PC+ABS, ECO-conforming flame retardant with metallic or pearlescent appearance.
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D792
Density 1.18 g/cc
0.0426 lb/in³
ISO 1183
1.20 g/cc
0.0434 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0030 - 0.0050 cm/cm

@Thickness 3.20 mm
0.0030 - 0.0050 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 14 g/10 min

@Load 2.16 kg,
Temperature 260 °C
14 g/10 min

@Load 4.76 lb,
Temperature 500 °F
ASTM D1238
Melt Index of Compound 14 g/10 min

@Load 2.16 kg,
Temperature 260 °C
14 g/10 min

@Load 4.76 lb,
Temperature 500 °F
MVR [cm^3/10 min]; ISO 1133
22 g/10 min

@Load 5.00 kg,
Temperature 260 °C
22 g/10 min

@Load 11.0 lb,
Temperature 500 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 121
121
ISO 2039-2
Hardness, H358/30 99.0 MPa
14400 psi
ISO 2039-1
Tensile Strength at Break 45.0 MPa
6530 psi
50 mm/min; ISO 527
46.0 MPa
6670 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 55.0 MPa
7980 psi
50 mm/min; ISO 527
59.0 MPa
8560 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 15 %
15 %
50 mm/min; ISO 527
20 %
20 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 4.0 %
4.0 %
Type I, 50 mm/min; ASTM D638
5.0 %
5.0 %
50 mm/min; ISO 527
Tensile Modulus 2.40 GPa
348 ksi
1 mm/min; ISO 527
3.10 GPa
450 ksi
50 mm/min; ASTM D638
Flexural Yield Strength 82.0 MPa
11900 psi
2 mm/min; ISO 178
94.0 MPa
13600 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.40 GPa
348 ksi
2 mm/min; ISO 178
2.68 GPa
389 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 1.60 J/cm
3.00 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 24.0 kJ/m²
11.4 ft-lb/in²
80*10*4; ISO 180/1A
12.0 kJ/m²

@Temperature -30.0 °C
5.71 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 2.50 J/cm²
11.9 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
1.30 J/cm²

@Temperature -30.0 °C
6.19 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 47.0 J

@Temperature 23.0 °C
34.7 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
40.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
80.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
44.4 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
CTE, linear, Transverse to Flow 72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
40.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
80.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
44.4 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
Thermal Conductivity 0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 0.46 MPa (66 psi) 128 °C
262 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
90.0 °C

@Thickness 3.20 mm
194 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 108 °C
226 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
82.0 °C

@Thickness 3.20 mm
180 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 98.0 °C
208 °F
Rate B/50; ASTM D1525
128 °C
262 °F
Rate B/50; ISO 306
130 °C
266 °F
Rate B/120; ISO 306
UL RTI, Electrical 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical with Impact 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical without Impact 60.0 °C
140 °F
UL 746B
Flammability, UL94 V-2

@Thickness 1.01 mm
V-2

@Thickness 0.0398 in
UL 94
V-1

@Thickness 1.19 mm
V-1

@Thickness 0.0469 in
UL 94
V-0

@Thickness 1.49 mm
V-0

@Thickness 0.0587 in
UL 94
5VB

@Thickness 2.00 mm
5VB

@Thickness 0.0787 in
UL 94
Oxygen Index 23 %
23 %
ISO 4589
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 2.7

@Frequency 1.00e+6 Hz
2.7

@Frequency 1.00e+6 Hz
IEC 60250
2.8

@Frequency 50.0 - 60.0 Hz
2.8

@Frequency 50.0 - 60.0 Hz
IEC 60250
Dielectric Strength 17.0 kV/mm

@Thickness 3.20 mm
432 kV/in

@Thickness 0.126 in
in oil; IEC 60243-1
25.0 kV/mm

@Thickness 1.60 mm
635 kV/in

@Thickness 0.0630 in
in oil; IEC 60243-1
35.0 kV/mm

@Thickness 0.800 mm
889 kV/in

@Thickness 0.0315 in
in oil; IEC 60243-1
Dissipation Factor 0.0030

@Frequency 50.0 - 60.0 Hz
0.0030

@Frequency 50.0 - 60.0 Hz
IEC 60250
0.0050

@Frequency 1.00e+6 Hz
0.0050

@Frequency 1.00e+6 Hz
IEC 60250
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES
IEC 60695-10-2