SABIC Innovative Plastics Cycoloy® EFX830ME PC (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® EFX830ME PC (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Modified PC blend offering metallic look with minimal flow lines, flame retarded without using Chlorinated or Brominated additives.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D 792
Density 1.19 g/cc
0.0430 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.10 %
0.10 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.25 %

@Temperature 23.0 °C
 0.25 %

@Temperature 73.4 °F
 ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0060 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0060 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 7.0 g/10 min

@Load 2.16 kg,
Temperature 260 °C
 7.0 g/10 min

@Load 4.76 lb,
Temperature 500 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
8.0 g/10 min

@Load 2.16 kg,
Temperature 260 °C
 8.0 g/10 min

@Load 4.76 lb,
Temperature 500 °F
 ASTM D 1238
15 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 15 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 ASTM D 1238
Mechanical Properties Metric English Comments
Hardness, Rockwell L 93
93
ISO 2039-2
Tensile Strength at Break 60.0 MPa
8700 psi
Type I, 50 mm/min; ASTM D 638
60.0 MPa
8700 psi
50 mm/min; ISO 527
Tensile Strength, Yield 62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D 638
62.0 MPa
8990 psi
50 mm/min; ISO 527
Elongation at Break 5.0 %
5.0 %
Type I, 50 mm/min; ASTM D 638
5.0 %
5.0 %
50 mm/min; ISO 527
Elongation at Yield 4.0 %
4.0 %
Type I, 50 mm/min; ASTM D 638
4.0 %
4.0 %
50 mm/min; ISO 527
Tensile Modulus 2.70 GPa
392 ksi
5 mm/min; ASTM D 638
2.70 GPa
392 ksi
1 mm/min; ISO 527
Flexural Yield Strength 97.0 MPa
14100 psi
2 mm/min; ISO 178
>= 100 MPa
>= 14500 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.30 GPa
334 ksi
1.3 mm/min, 50 mm span; ASTM D 790
2.40 GPa
348 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.550 J/cm

@Temperature -30.0 °C
 1.03 ft-lb/in

@Temperature -22.0 °F
 ASTM D 256
0.650 J/cm

@Temperature 23.0 °C
 1.22 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 5.00 J/cm

@Temperature 23.0 °C
 9.37 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature -30.0 °C
 2.38 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
6.00 kJ/m²

@Temperature 23.0 °C
 2.86 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 31.0 kJ/m²

@Temperature 23.0 °C
 14.8 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Charpy Impact Unnotched 4.40 J/cm²

@Temperature 23.0 °C
 20.9 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/2C
Charpy Impact, Notched 0.600 J/cm²

@Temperature -30.0 °C
 2.86 ft-lb/in²

@Temperature -22.0 °F
 V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.700 J/cm²

@Temperature 23.0 °C
 3.33 ft-lb/in²

@Temperature 73.4 °F
 V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 16.0 J

@Temperature 23.0 °C
 11.8 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 38.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 38.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 38.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 38.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Thermal Conductivity 0.250 W/m-K
1.74 BTU-in/hr-ft²-°F
ASTM E 1530
Deflection Temperature at 1.8 MPa (264 psi) 86.0 °C
187 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
87.0 °C

@Thickness 3.20 mm
 189 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Vicat Softening Point 103 °C
217 °F
Rate B/50; ASTM D 1525
103 °C
217 °F
Rate B/50; ISO 306
105 °C
221 °F
Rate B/120; ISO 306
111 °C
232 °F
Rate A/50; ISO 306
111 °C
232 °F
Rate A/50; ASTM D 1525
Flammability, UL94 V-1

@Thickness 1.20 mm
 V-1

@Thickness 0.0472 in
 UL 94
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
 UL 94
5VB

@Thickness 2.00 mm
 5VB

@Thickness 0.0787 in
 UL 94
5VA

@Thickness 3.50 mm
 5VA

@Thickness 0.138 in
 UL 94
Glow Wire Test 800 °C

@Thickness 1.00 mm
 1470 °F

@Thickness 0.0394 in
 Glow Wire Ignitability Temperature; IEC 60695-2-13
960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 Glow Wire Flammability Index; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
ASTM D 257
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ASTM D 257
Dielectric Constant 2.9

@Frequency 50.0 - 60.0 Hz
 2.9

@Frequency 50.0 - 60.0 Hz
 ASTM D 150
2.9

@Frequency 1.00e+6 Hz
 2.9

@Frequency 1.00e+6 Hz
 ASTM D 150
Dielectric Strength 23.0 kV/mm

@Thickness 1.60 mm
 584 kV/in

@Thickness 0.0630 in
 in oil; ASTM D 149
Dissipation Factor 0.0040

@Frequency 1.00e+6 Hz
 0.0040

@Frequency 1.00e+6 Hz
 ASTM D 150
0.020

@Frequency 50.0 - 60.0 Hz
 0.020

@Frequency 50.0 - 60.0 Hz
 ASTM D 150
Descriptive Properties Value Comments
Ball Pressure Test, 75°C +/- 2°C PASS
IEC 60695-10-2