SABIC Innovative Plastics Cycoloy® CY6110 PC+ABS (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® CY6110 PC+ABS (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering hydrolytic stability and excellent flow / impact balance for a wide variety of thin wall or large size applications including business equipment, enclosures, among others.
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
ISO 1183
Moisture Absorption 0.200 %
0.200 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.60 %
0.60 %
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0060 in/in

@Thickness 0.126 in
SABIC Method
Melt Index of Compound 23 g/10 min

@Load 2.16 kg,
Temperature 260 °C
23 g/10 min

@Load 4.76 lb,
Temperature 500 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 46.0 MPa
6670 psi
50 mm/min; ISO 527
47.0 MPa
6820 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 63.0 MPa
9140 psi
50 mm/min; ISO 527
63.0 MPa
9140 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 35 %
35 %
50 mm/min; ISO 527
65 %
65 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 4.0 %
4.0 %
50 mm/min; ISO 527
4.1 %
4.1 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.75 GPa
399 ksi
1 mm/min; ISO 527
2.76 GPa
400 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 94.0 MPa
13600 psi
2 mm/min; ISO 178
Flexural Modulus 2.44 GPa
354 ksi
2 mm/min; ISO 178
Izod Impact, Notched 4.75 J/cm
8.90 ft-lb/in
ASTM D256
1.00 J/cm

@Temperature -30.0 °C
1.87 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 23.0 kJ/m²
10.9 ft-lb/in²
80*10*4; ISO 180/1A
45.0 kJ/m²
21.4 ft-lb/in²
80*10*3; ISO 180/1A
10.0 kJ/m²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
12.0 kJ/m²

@Temperature -30.0 °C
5.71 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 3.30 J/cm²
15.7 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
4.50 J/cm²
21.4 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
1.00 J/cm²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
44.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
44.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 98.0 °C
208 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 88.0 °C
190 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
Vicat Softening Point 104 °C
219 °F
Rate B/50; ISO 306
106 °C
223 °F
Rate B/120; ISO 306
UL RTI, Electrical 85.0 °C
185 °F
UL 746B
UL RTI, Mechanical with Impact 85.0 °C
185 °F
UL 746B
UL RTI, Mechanical without Impact 85.0 °C
185 °F
UL 746B
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL 94 by SABIC-IP
V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL 94
5VB

@Thickness 2.50 mm
5VB

@Thickness 0.0984 in
UL 94
Oxygen Index 31 %
31 %
ISO 4589
Glow Wire Test 775 °C
1430 °F
IEC 60695-2-13
775 °C
1430 °F
IEC 60695-2-13
775 °C
1430 °F
IEC 60695-2-13
825 °C
1520 °F
IEC 60695-2-13
825 °C
1520 °F
IEC 60695-2-13
825 °C
1520 °F
IEC 60695-2-13
960 °C

@Thickness 1.00 mm
1760 °F

@Thickness 0.0394 in
IEC 60695-2-12
960 °C

@Thickness 0.750 mm
1760 °F

@Thickness 0.0295 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 2.9

@Frequency 1.00e+6 Hz
2.9

@Frequency 1.00e+6 Hz
IEC 60250
2.9

@Frequency 50.0 - 60.0 Hz
2.9

@Frequency 50.0 - 60.0 Hz
IEC 60250
Dielectric Strength 31.0 kV/mm

@Thickness 1.60 mm
787 kV/in

@Thickness 0.0630 in
in oil; IEC 60243-1
46.0 kV/mm

@Thickness 0.800 mm
1170 kV/in

@Thickness 0.0315 in
in oil; IEC 60243-1
Dissipation Factor 0.0020

@Frequency 50.0 - 60.0 Hz
0.0020

@Frequency 50.0 - 60.0 Hz
IEC 60250
0.0070

@Frequency 1.00e+6 Hz
0.0070

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 250 - 400 V
250 - 400 V
UL 746A
Hot Wire Ignition, HWI 15 - 30 sec
15 - 30 sec
UL 746A
Descriptive Properties Value Comments
Ball Pressure Test, 75°C +/- 2°C PASS
IEC 60695-10-2