SABIC Innovative Plastics Cycoloy® CY6010 PC+ABS (Asia Pacific)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® CY6010 PC+ABS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Cycoloy CY6010 resin is a flame retardant PC/ABS blend featuring excellent flow together with good impact and UL-94 V0 listing at 1.5mm. Its excellent flow combined with balanced heat and good practical impact makes it an ideal candidate for a wide variety of applications.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D 792
Density 1.18 g/cc
0.0426 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.050 %
0.050 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.10 %

@Temperature 23.0 °C
0.10 %

@Temperature 73.4 °F
ISO 62
Viscosity 100000 cP

@Temperature 260 °C
100000 cP

@Temperature 500 °F
melt; 1500 sec-1; ISO 11443
Linear Mold Shrinkage, Flow 0.0043 - 0.0047 cm/cm

@Thickness 3.20 mm
0.0043 - 0.0047 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 30 g/10 min

@Load 2.16 kg,
Temperature 260 °C
30 g/10 min

@Load 4.76 lb,
Temperature 500 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
34 g/10 min

@Load 2.16 kg,
Temperature 260 °C
34 g/10 min

@Load 4.76 lb,
Temperature 500 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 43.0 MPa
6240 psi
50 mm/min; ISO 527
48.0 MPa
6960 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 63.0 MPa
9140 psi
Type I, 50 mm/min; ASTM D 638
63.0 MPa
9140 psi
50 mm/min; ISO 527
Elongation at Break 34 %
34 %
Type I, 50 mm/min; ASTM D 638
40 %
40 %
50 mm/min; ISO 527
Elongation at Yield 4.0 %
4.0 %
Type I, 50 mm/min; ASTM D 638
4.0 %
4.0 %
50 mm/min; ISO 527
Tensile Modulus 2.67 GPa
387 ksi
1 mm/min; ISO 527
2.79 GPa
405 ksi
5 mm/min; ASTM D 638
Flexural Yield Strength 95.0 MPa
13800 psi
2 mm/min; ISO 178
97.0 MPa
14100 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.63 GPa
381 ksi
1.3 mm/min, 50 mm span; ASTM D 790
2.65 GPa
384 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.650 J/cm

@Temperature -30.0 °C
1.22 ft-lb/in

@Temperature -22.0 °F
ASTM D 256
0.920 J/cm

@Temperature 23.0 °C
1.72 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
10.0 kJ/m²

@Temperature 23.0 °C
4.76 ft-lb/in²

@Temperature 73.4 °F
80*10*3; ISO 180/1A
Charpy Impact, Notched 0.500 J/cm²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
1.00 J/cm²

@Temperature 23.0 °C
4.76 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
Impact Test 20.0 J

@Temperature 23.0 °C
14.8 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 71.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
39.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
73.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
40.6 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
40.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
78.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
43.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 73.0 °C
163 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
81.0 °C

@Thickness 3.20 mm
178 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Vicat Softening Point 88.0 °C
190 °F
Rate B/50; ISO 306
92.0 °C
198 °F
Rate B/120; ISO 306
Flammability, UL94 V-1

@Thickness 1.00 mm
V-1

@Thickness 0.0394 in
UL 94 by SABIC-IP
V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL 94 by SABIC-IP