SABIC Innovative Plastics Cycoloy® CY4000M PC+ABS (Asia Pacific)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® CY4000M PC+ABS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Cycoloy* CY4000M resin is an injection moldable, flame retardant PC/ABS blend free of chlorinated or brominated flame resistant additives. Cycoloy CY4000M resin has excellent flow and balanced impact properties and is available in various color options. It is an ideal candidate for a wide variety of different applications.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Moisture Absorption 0.200 %
0.200 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.60 %
0.60 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 25 g/10 min

@Load 2.16 kg,
Temperature 260 °C
25 g/10 min

@Load 4.76 lb,
Temperature 500 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 46.0 MPa
6670 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 60.0 MPa
8700 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 44 %
44 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 4.0 %
4.0 %
Type I, 50 mm/min; ASTM D638
Flexural Yield Strength 93.0 MPa
13500 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.40 GPa
348 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 5.50 J/cm
10.3 ft-lb/in
ASTM D256
1.20 J/cm

@Temperature -30.0 °C
2.25 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Dart Drop, Total Energy 55.0 J

@Temperature 23.0 °C
40.6 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
44.4 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
44.4 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 80.0 °C

@Thickness 3.20 mm
176 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 98.0 °C
208 °F
Rate B/50; ASTM D1525
98.0 °C
208 °F
Rate B/50; ISO 306
100 °C
212 °F
Rate B/120; ISO 306
Flammability, UL94 V-0

@Thickness 2.50 mm
V-0

@Thickness 0.0984 in
UL 94 by SABIC-IP