SABIC Innovative Plastics Cycoloy® CX7259 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycoloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycoloy® CX7259 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Cycoloy resin grade CX7259 is a flame retardant impact modified polycarbonate blend aiming at ultra thin wall designs. It is listed as UL-94 V1 at 0.5mm & V0 at 0.6mm with excellent flow and balanced heat resistance ideally for many thin wall applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.100 % | 0.100 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.17 % | 0.17 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 23 g/10 min @Load 2.16 kg, Temperature 260 °C |
23 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D1238 |
| Melt Index of Compound | 19 g/10 min @Load 2.16 kg, Temperature 260 °C |
19 g/10 min @Load 4.76 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 28 g/10 min @Load 1.20 kg, Temperature 300 °C |
28 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 49.0 MPa | 7110 psi | 50 mm/min; ISO 527 |
| 53.0 MPa | 7690 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 59.0 MPa | 8560 psi | Type I, 50 mm/min; ASTM D638 |
| 64.0 MPa | 9280 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 70 % | 70 % | 50 mm/min; ISO 527 |
| 80 % | 80 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 3.8 % | 3.8 % | Type I, 50 mm/min; ASTM D638 |
| 3.8 % | 3.8 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.60 GPa | 377 ksi | 1 mm/min; ISO 527 |
| 2.63 GPa | 381 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 96.0 MPa | 13900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 98.0 MPa | 14200 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 2.62 GPa | 380 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.67 GPa | 387 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.27 J/cm | 2.38 ft-lb/in | ASTM D256 |
| 0.690 J/cm @Temperature -30.0 °C |
1.29 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*3; ISO 180/1A |
| 9.00 kJ/m² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*3; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | NB | NB | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 0.900 J/cm² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 70.0 J @Temperature 23.0 °C |
51.6 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 69.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 72.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 73.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 93.0 °C @Thickness 6.40 mm |
199 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 101 °C | 214 °F | Rate B/50; ASTM D1525 |
| 101 °C | 214 °F | Rate B/50; ISO 306 | |
| 104 °C | 219 °F | Rate B/120; ISO 306 | |
| Flammability, UL94 | V-2 @Thickness 0.300 mm |
V-2 @Thickness 0.0118 in |
UL 94 |
| V-1 @Thickness 0.500 mm |
V-1 @Thickness 0.0197 in |
UL 94 | |
| V-0 @Thickness 0.600 mm |
V-0 @Thickness 0.0236 in |
UL 94 |