SABIC Innovative Plastics Cycoloy® CX7240U PC+ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycoloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycoloy® CX7240U PC+ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Cycoloy* CX7240U resin is an injection moldable PC/ABS blend with a UV stabilization package. It contains non-brominated and non-chlorinated flame retardant systems to meet thin wall flame resistance. Excellent flow and impact balance together with the thin wall flame resistance and all color options make Cycoloy CX7240U an ideal candidate for a wide variety of thin wall applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.100 % | 0.100 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.20 % | 0.20 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 16 g/10 min @Load 2.16 kg, Temperature 260 °C |
16 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D1238 |
| Melt Index of Compound | 15 g/10 min @Load 2.16 kg, Temperature 260 °C |
15 g/10 min @Load 4.76 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 |
| 58.0 MPa | 8410 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | Type I, 50 mm/min; ASTM D638 |
| 65.0 MPa | 9430 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 90 % | 90 % | 50 mm/min; ISO 527 |
| 100 % | 100 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| 4.1 % | 4.1 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 2.53 GPa | 367 ksi | 1 mm/min; ISO 527 |
| 2.95 GPa | 428 ksi | 50 mm/min; ASTM D638 | |
| Flexural Yield Strength | 96.0 MPa | 13900 psi | 2 mm/min; ISO 178 |
| 104 MPa | 15100 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.50 GPa | 363 ksi | 2 mm/min; ISO 178 |
| 2.75 GPa | 399 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 5.00 J/cm | 9.37 ft-lb/in | ASTM D256 |
| 1.00 J/cm @Temperature -30.0 °C |
1.87 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | 80*10*3; ISO 180/1A |
| 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A | |
| Charpy Impact, Notched | 2.00 J/cm² | 9.52 ft-lb/in² | Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 65.0 J @Temperature 23.0 °C |
47.9 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 62.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
34.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 62.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
34.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 53.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
29.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 54.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
30.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C @Thickness 3.20 mm |
212 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 89.0 °C @Thickness 3.20 mm |
192 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| 99.0 °C @Thickness 6.40 mm |
210 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 106 °C | 223 °F | Rate B/50; ASTM D1525 |
| 110 °C | 230 °F | Rate B/50; ISO 306 | |
| 113 °C | 235 °F | Rate B/120; ISO 306 | |
| UL RTI, Electrical | 90.0 °C | 194 °F | UL 746B |
| UL RTI, Mechanical with Impact | 90.0 °C | 194 °F | UL 746B |
| UL RTI, Mechanical without Impact | 90.0 °C | 194 °F | UL 746B |
| Flammability, UL94 | V-2 @Thickness 0.400 mm |
V-2 @Thickness 0.0157 in |
UL 94 |
| V-1 @Thickness 0.600 mm |
V-1 @Thickness 0.0236 in |
UL 94 | |
| V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
UL 94 | |
| 5VB @Thickness 1.50 mm |
5VB @Thickness 0.0591 in |
UL 94 | |
| 5VA @Thickness 3.00 mm |
5VA @Thickness 0.118 in |
UL 94 | |
| Glow Wire Test | 800 °C | 1470 °F | IEC 60695-2-13 |
| 825 °C | 1520 °F | IEC 60695-2-13 | |
| 960 °C @Thickness 0.750 mm |
1760 °F @Thickness 0.0295 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | UL 746A |
| Hot Wire Ignition, HWI | 15 - 30 sec | 15 - 30 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 75°C +/- 2°C | PASS | IEC 60695-10-2 |