SABIC Innovative Plastics Cycoloy® CX1440 PC+ABS (Asia Pacific)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® CX1440 PC+ABS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
CYCOLOY CX1440 is a general purpose PC+ABS blend specially developped for thin wall applications requiring weld line strength and high flow with a good balance of properties
Physical Properties Metric English Comments
Specific Gravity 1.15 g/cc
1.15 g/cc
ASTM D792
Density 1.15 g/cc
0.0415 lb/in³
ISO 1183
Moisture Absorption 0.160 %
0.160 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.60 %
0.60 %
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0060 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 22 g/10 min

@Load 5.00 kg,
Temperature 260 °C
22 g/10 min

@Load 11.0 lb,
Temperature 500 °F
ASTM D1238
Melt Index of Compound 20 g/10 min

@Load 5.00 kg,
Temperature 260 °C
20 g/10 min

@Load 11.0 lb,
Temperature 500 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell L 90
90
ISO 2039-2
Tensile Strength at Break 45.0 MPa
6530 psi
50 mm/min; ISO 527
45.0 MPa
6530 psi
5 mm/min; ISO 527
45.0 MPa
6530 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 45.0 MPa
6530 psi
5 mm/min; ISO 527
50.0 MPa
7250 psi
Type I, 50 mm/min; ASTM D638
50.0 MPa
7250 psi
50 mm/min; ISO 527
Elongation at Break 45 %
45 %
Type I, 50 mm/min; ASTM D638
50 %
50 %
50 mm/min; ISO 527
60 %
60 %
5 mm/min; ISO 527
Elongation at Yield 5.0 %
5.0 %
50 mm/min; ISO 527
5.0 %
5.0 %
5 mm/min; ISO 527
5.0 %
5.0 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.40 GPa
348 ksi
1 mm/min; ISO 527
2.40 GPa
348 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 80.0 MPa
11600 psi
2 mm/min; ISO 178
80.0 MPa
11600 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.30 GPa
334 ksi
2 mm/min; ISO 178
2.30 GPa
334 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 1.00 J/cm
1.87 ft-lb/in
Izod Impact, double-gated, 23°C; SABIC Method
4.50 J/cm
8.43 ft-lb/in
ASTM D256
2.50 J/cm

@Temperature -30.0 °C
4.68 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 40.0 kJ/m²
19.0 ft-lb/in²
80*10*3; ISO 180/1A
20.0 kJ/m²

@Temperature -30.0 °C
9.52 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
Charpy Impact, Notched 4.00 J/cm²
19.0 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
2.00 J/cm²

@Temperature -30.0 °C
9.52 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 25.0 J

@Temperature -30.0 °C
18.4 ft-lb

@Temperature -22.0 °F
ASTM D3763
55.0 J

@Temperature 23.0 °C
40.6 ft-lb

@Temperature 73.4 °F
ASTM D3763
Impact Test 70.0 J
51.6 ft-lb
Multiaxial Impact; ISO 6603
Taber Abrasion, mg/1000 Cycles 70
70
CS-17, 1 kg; SABIC Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 71.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
39.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
75.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.7 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 73.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
40.6 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
77.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
42.8 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Thermal Conductivity 0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
ASTM C177
0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
ISO 8302
Hot Ball Pressure Test <= 100 °C
<= 212 °F
IEC 60695-10-2
Deflection Temperature at 0.46 MPa (66 psi) 117 °C
243 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
115 °C

@Thickness 3.20 mm
239 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 95.0 °C
203 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
95.0 °C

@Thickness 3.20 mm
203 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 113 °C
235 °F
Rate B/50; ASTM D1525
114 °C
237 °F
Rate B/50; ISO 306
116 °C
241 °F
Rate B/120; ISO 306
UL RTI, Electrical 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical with Impact 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical without Impact 60.0 °C
140 °F
UL 746B
Flammability, UL94 HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
UL 94
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
UL 94
Glow Wire Test 650 °C

@Thickness 3.20 mm
1200 °F

@Thickness 0.126 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
ASTM D257
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ASTM D257
Dielectric Constant 2.7

@Frequency 1.00e+6 Hz
2.7

@Frequency 1.00e+6 Hz
IEC 60250
2.9

@Frequency 50.0 - 60.0 Hz
2.9

@Frequency 50.0 - 60.0 Hz
IEC 60250
Dielectric Strength 27.0 kV/mm

@Thickness 1.60 mm
686 kV/in

@Thickness 0.0630 in
in oil; IEC 60243-1
36.0 kV/mm

@Thickness 0.800 mm
914 kV/in

@Thickness 0.0315 in
in oil; IEC 60243-1
Dissipation Factor 0.010

@Frequency 50.0 - 60.0 Hz
0.010

@Frequency 50.0 - 60.0 Hz
IEC 60250
0.011

@Frequency 1.00e+6 Hz
0.011

@Frequency 1.00e+6 Hz
IEC 60250
Descriptive Properties Value Comments
Ball Pressure Test, 75°C +/- 2°C passes
IEC 60695-10-2