SABIC Innovative Plastics Cycoloy® CS9610 PC+ABS

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® CS9610 PC+ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Cycoloy* CS9610 is a FR PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering optimum mechanical & impact balance and excellent flammability and low smoke behavior. This grade potentially can be considered for a wide variety of applications in areas such as transportation, consumer electronics and electrical equipments.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0060 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 15 g/10 min

@Load 5.00 kg,
Temperature 260 °C
15 g/10 min

@Load 11.0 lb,
Temperature 500 °F
ASTM D1238
Melt Index of Compound 12 g/10 min

@Load 5.00 kg,
Temperature 260 °C
12 g/10 min

@Load 11.0 lb,
Temperature 500 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.0 MPa
7250 psi
50 mm/min; ISO 527
62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 62.0 MPa
8990 psi
50 mm/min; ISO 527
64.0 MPa
9280 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break >= 45 %
>= 45 %
50 mm/min; ISO 527
55 %
55 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 4.8 %
4.8 %
50 mm/min; ISO 527
5.0 %
5.0 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.40 GPa
348 ksi
1 mm/min; ISO 527
2.60 GPa
377 ksi
50 mm/min; ASTM D638
Flexural Yield Strength 98.0 MPa
14200 psi
1.3 mm/min, 50 mm span; ASTM D790
98.0 MPa
14200 psi
2 mm/min; ISO 178
Flexural Modulus 2.44 GPa
354 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.50 GPa
363 ksi
2 mm/min; ISO 178
Izod Impact, Notched 8.00 J/cm
15.0 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 45.0 kJ/m²
21.4 ft-lb/in²
80*10*3; ISO 180/1A
15.0 kJ/m²

@Temperature -30.0 °C
7.14 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
Charpy Impact, Notched 4.50 J/cm²
21.4 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
1.50 J/cm²

@Temperature -30.0 °C
7.14 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 72.0 J

@Temperature 23.0 °C
53.1 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 118 °C

@Thickness 3.20 mm
244 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 106 °C
223 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
105 °C

@Thickness 3.20 mm
221 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 124 °C
255 °F
Rate B/50; ISO 306
127 °C
261 °F
Rate B/120; ISO 306
Flammability, UL94 V-0

@Thickness 2.00 mm
V-0

@Thickness 0.0787 in
UL 94
5VB

@Thickness 2.00 mm
5VB

@Thickness 0.0787 in
UL 94
Descriptive Properties Value Comments
NBS Smoke Density, Flaming, Dmax 225
ASTM E 662
NBS Smoke Density, Flaming, Ds 1.5 min 40
ASTM E 662
NBS Smoke Density, Flaming, Ds 4 min 150
ASTM E 662