SABIC Innovative Plastics Cycoloy® CM6220 PC (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® CM6220 PC (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
CYCOLOY CM6220 resin is a mineral filled grade featuring of high modulus (6GPa), good flow and ductility, low warpage. It is of non-Br & non-Cl flame retardant systems intended to meet thin wall flame resistance and various environmental requirements.
Physical Properties Metric English Comments
Specific Gravity 1.39 g/cc
1.39 g/cc
ASTM D792
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0020 - 0.0030 cm/cm

@Thickness 3.20 mm
0.0020 - 0.0030 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 12 g/10 min

@Load 2.16 kg,
Temperature 260 °C
12 g/10 min

@Load 4.76 lb,
Temperature 500 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 109
109
ASTM D785
Tensile Strength at Break 30.0 MPa
4350 psi
5 mm/min; ISO 527
34.0 MPa
4930 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 55.0 MPa
7980 psi
Type I, 5 mm/min; ASTM D638
56.0 MPa
8120 psi
5 mm/min; ISO 527
Elongation at Break 6.0 %
6.0 %
5 mm/min; ISO 527
15 %
15 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 3.0 %
3.0 %
Type I, 5 mm/min; ASTM D638
3.0 %
3.0 %
5 mm/min; ISO 527
Tensile Modulus 5.57 GPa
808 ksi
1 mm/min; ISO 527
5.85 GPa
848 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 98.0 MPa
14200 psi
1.3 mm/min, 50 mm span; ASTM D790
98.0 MPa
14200 psi
2 mm/min; ISO 178
Flexural Modulus 6.03 GPa
875 ksi
1.3 mm/min, 50 mm span; ASTM D790
6.15 GPa
892 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.950 J/cm
1.78 ft-lb/in
ASTM D256
0.520 J/cm

@Temperature -30.0 °C
0.974 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 30.0 J

@Temperature 23.0 °C
22.1 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 34.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
18.9 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
CTE, linear, Transverse to Flow 72.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
40.0 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 92.0 °C

@Thickness 3.20 mm
198 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 87.0 °C
189 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
85.0 °C

@Thickness 3.20 mm
185 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 98.0 °C
208 °F
Rate B/50; ASTM D1525
Flammability, UL94 V-1

@Thickness 0.800 mm
V-1

@Thickness 0.0315 in
UL 94
V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL 94
5VB

@Thickness 1.50 mm
5VB

@Thickness 0.0591 in
UL 94