Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® CH6410 PC+ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
CH6410 is a high heat, impact modified PC resin, with nonbrominated, nonchlorinated flame retardant system. Limited colors only.
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D792
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.00050 - 0.00070 cm/cm
0.00050 - 0.00070 in/in
on Tensile Bar; SABIC Method
0.0040 - 0.0050 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0050 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 6.3 g/10 min

@Load 2.16 kg,
Temperature 260 °C
6.3 g/10 min

@Load 4.76 lb,
Temperature 500 °F
ASTM D1238
Melt Index of Compound 16 g/10 min

@Load 5.00 kg,
Temperature 260 °C
16 g/10 min

@Load 11.0 lb,
Temperature 500 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, H358/30 100 MPa
14500 psi
ISO 2039-1
Tensile Strength at Break 54.0 MPa
7830 psi
Type I, 50 mm/min; ASTM D638
55.0 MPa
7980 psi
50 mm/min; ISO 527
Tensile Strength, Yield 63.0 MPa
9140 psi
Type I, 50 mm/min; ASTM D638
63.0 MPa
9140 psi
50 mm/min; ISO 527
Elongation at Break 88 %
88 %
Type I, 50 mm/min; ASTM D638
95 %
95 %
50 mm/min; ISO 527
Elongation at Yield 5.0 %
5.0 %
50 mm/min; ISO 527
5.5 %
5.5 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.30 GPa
334 ksi
1 mm/min; ISO 527
2.54 GPa
368 ksi
50 mm/min; ASTM D638
Flexural Yield Strength 90.0 MPa
13100 psi
2 mm/min; ISO 178
95.0 MPa
13800 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.40 GPa
348 ksi
2 mm/min; ISO 178
2.59 GPa
376 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 9.07 J/cm
17.0 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 50.0 kJ/m²
23.8 ft-lb/in²
80*10*4; ISO 180/1A
15.0 kJ/m²

@Temperature -30.0 °C
7.14 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
19.0 kJ/m²

@Temperature 0.000 °C
9.04 ft-lb/in²

@Temperature 32.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 5.50 J/cm²
26.2 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
1.50 J/cm²

@Temperature -30.0 °C
7.14 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 72.0 J

@Temperature 23.0 °C
53.1 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
38.9 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
77.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
43.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 59.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
70.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
38.9 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 126 °C
259 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
127 °C

@Thickness 3.20 mm
261 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 113 °C
235 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
118 °C

@Thickness 3.20 mm
244 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 134 °C
273 °F
Rate B/50; ISO 306
135 °C
275 °F
Rate B/120; ISO 306
Flammability, UL94 V-1

@Thickness 0.990 mm
V-1

@Thickness 0.0390 in
UL 94
V-0

@Thickness 1.49 mm
V-0

@Thickness 0.0587 in
UL 94
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 2.7

@Frequency 1.00e+6 Hz
2.7

@Frequency 1.00e+6 Hz
IEC 60250
2.7

@Frequency 50.0 - 60.0 Hz
2.7

@Frequency 50.0 - 60.0 Hz
IEC 60250
Dielectric Strength 18.0 kV/mm

@Thickness 3.20 mm
457 kV/in

@Thickness 0.126 in
in oil; IEC 60243-1
Dissipation Factor 0.0010

@Frequency 50.0 - 60.0 Hz
0.0010

@Frequency 50.0 - 60.0 Hz
IEC 60250
0.010

@Frequency 1.00e+6 Hz
0.010

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 225 V
225 V
IEC 60112
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES
IEC 60695-10-2