SABIC Innovative Plastics Cycoloy® C7122 PC+ABS (Asia Pacific)
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycoloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycoloy® C7122 PC+ABS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Cycoloy*C7122 is a mineral filled, non-halogenated flame retardant PC/ABS. Good stiffness with balanced flow and impact performance.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ASTM D792 |
| Water Absorption | 0.20 % @Time 86400 sec |
0.20 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0040 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 13 g/10 min @Load 2.16 kg, Temperature 260 °C |
13 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 40.0 MPa | 5800 psi | Type I, 5 mm/min; ASTM D638 |
| 94.0 MPa | 13600 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 59.0 MPa | 8560 psi | SABIC - Japan Method |
| 60.0 MPa | 8700 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 6.6 % | 6.6 % | 5 mm/min; ISO 527 |
| 90 % | 90 % | SABIC - Japan Method | |
| Tensile Modulus | 4.09 GPa | 593 ksi | 1 mm/min; ISO 527 |
| 4.23 GPa | 614 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 95.0 MPa | 13800 psi | ASTM D790 |
| Flexural Yield Strength | 95.0 MPa | 13800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 96.0 MPa | 13900 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 3.96 GPa | 574 ksi | ASTM D790 |
| 3.96 GPa | 574 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 4.15 GPa | 602 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.39 J/cm | 2.60 ft-lb/in | ASTM D256 |
| 0.570 J/cm @Temperature -30.0 °C |
1.07 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 65.0 J @Temperature 23.0 °C |
47.9 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 50.0 - 70.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
27.8 - 38.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| CTE, linear, Parallel to Flow | 61.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 49.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C @Thickness 3.20 mm |
196 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 85.0 °C @Thickness 6.40 mm |
185 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 92.0 °C | 198 °F | Rate B/50; ISO 306 |
| 93.0 °C | 199 °F | Rate B/120; ISO 306 | |
| Flammability, UL94 | V-1 @Thickness 1.20 mm |
V-1 @Thickness 0.0472 in |
UL 94 |
| V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 | |
| 5VB @Thickness 1.80 mm |
5VB @Thickness 0.0709 in |
UL 94 |