SABIC Innovative Plastics Cycoloy® C4210 PC+ABS (Europe-Africa-Middle East)

Category	Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	Cycoloy®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics Cycoloy® C4210 PC+ABS (Europe-Africa-Middle East).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

CYCOLOY C4210 is a 10% glass reinforced, non-FR PC+ABS grade. It shows high heat resistance, excellent strength and rigidity with good cosmetic appearance. It combines a good processabity with a low shrinkage.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.

Physical Properties	Metric	English	Comments
Density	1.22 g/cc	0.0441 lb/in³	ISO 1183
Moisture Absorption at Equilibrium	0.20 %	0.20 %	23°C / 50% RH; ISO 62
Water Absorption at Saturation	0.60 % @Temperature 23.0 °C	0.60 % @Temperature 73.4 °F	ISO 62
Linear Mold Shrinkage, Flow	0.0030 - 0.0050 cm/cm	0.0030 - 0.0050 in/in	on tensile bar; SABIC Method
Melt Flow	15 g/10 min @Load 5.00 kg, Temperature 260 °C	15 g/10 min @Load 11.0 lb, Temperature 500 °F	[cm^3/10 min] Melt Volume Rate; ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	121	121	ISO 2039-2
Hardness, H358/30	116 MPa	16800 psi	ISO 2039-1
Tensile Strength at Break	70.0 MPa	10200 psi	5 mm/min; ISO 527
Tensile Strength, Yield	70.0 MPa	10200 psi	5 mm/min; ISO 527
Elongation at Break	3.5 %	3.5 %	5 mm/min; ISO 527
Elongation at Yield	3.5 %	3.5 %	5 mm/min; ISO 527
Tensile Modulus	4.00 GPa	580 ksi	1 mm/min; ISO 527
Flexural Strength	120 MPa	17400 psi	2 mm/min; ISO 178
Flexural Modulus	3.80 GPa	551 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	9.00 kJ/m² @Temperature -30.0 °C	4.28 ft-lb/in² @Temperature -22.0 °F	80104; ISO 180/1A
	11.0 kJ/m² @Temperature 23.0 °C	5.23 ft-lb/in² @Temperature 73.4 °F	80103; ISO 180/1A
	11.0 kJ/m² @Temperature 23.0 °C	5.23 ft-lb/in² @Temperature 73.4 °F	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	20.0 kJ/m² @Temperature 23.0 °C	9.52 ft-lb/in² @Temperature 73.4 °F	80103; ISO 180/1U
	35.0 kJ/m² @Temperature 23.0 °C	16.7 ft-lb/in² @Temperature 73.4 °F	80104; ISO 180/1U
Charpy Impact Unnotched	2.00 J/cm² @Temperature 23.0 °C	9.52 ft-lb/in² @Temperature 73.4 °F	Edgew 80103 sp=62mm; ISO 179/1eU
	3.50 J/cm² @Temperature 23.0 °C	16.7 ft-lb/in² @Temperature 73.4 °F	Edgew 80104 sp=62mm; ISO 179/1eU
Charpy Impact, Notched	0.900 J/cm² @Temperature -30.0 °C	4.28 ft-lb/in² @Temperature -22.0 °F	V-notch Edgew 80104 sp=62mm; ISO 179/1eA
	1.10 J/cm² @Temperature 23.0 °C	5.23 ft-lb/in² @Temperature 73.4 °F	V-notch Edgew 80103 sp=62mm; ISO 179/1eA
	1.10 J/cm² @Temperature 23.0 °C	5.23 ft-lb/in² @Temperature 73.4 °F	V-notch Edgew 80104 sp=62mm; ISO 179/1eA

Thermal Properties	Metric	English	Comments
Thermal Conductivity	0.200 W/m-K	1.39 BTU-in/hr-ft²-°F	ISO 8302
Deflection Temperature at 0.46 MPa (66 psi)	134 °C	273 °F	Edgew 120104 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi)	120 °C	248 °F	Edgew 120104 sp=100mm; ISO 75/Ae
Vicat Softening Point	134 °C	273 °F	Rate B/50; ISO 306
	136 °C	277 °F	Rate B/120; ISO 306
UL RTI, Electrical	60.0 °C	140 °F	UL 746B
UL RTI, Mechanical with Impact	60.0 °C	140 °F	UL 746B
UL RTI, Mechanical without Impact	60.0 °C	140 °F	UL 746B
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in	2nd value; UL 94 by SABIC-IP
	HB @Thickness 3.20 mm	HB @Thickness 0.126 in	UL 94 by SABIC-IP
Glow Wire Test	960 °C @Thickness 3.20 mm	1760 °F @Thickness 0.126 in	Glow Wire Flammability Index; IEC 60695-2-12

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm	IEC 60093
Surface Resistance	>= 1.00e+15 ohm	>= 1.00e+15 ohm	ROA; IEC 60093

Descriptive Properties	Value	Comments
Ball Pressure Test, 125°C +/- 2°C	PASSES	IEC 60695-10-2
Ball Pressure Test, 75°C +/- 2°C	PASSES	IEC 60695-10-2