SABIC Innovative Plastics Cycoloy® C1204HF PC+ABS (Asia Pacific)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® C1204HF PC+ABS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High heat PC/ABS blend offering good flow and excellent impact. Food compliant according to FDA and European directive 2002/72/EC. Available in limited colors. Effective January 15th, 2008 this grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility. Alternative grade HC1204HF.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.15 g/cc
1.15 g/cc
ASTM D 792
Density 1.15 g/cc
0.0415 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.60 %

@Temperature 23.0 °C
0.60 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
on tensile bar; SABIC Method
0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 8.0 g/10 min

@Load 2.16 kg,
Temperature 260 °C
8.0 g/10 min

@Load 4.76 lb,
Temperature 500 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
22 g/10 min

@Load 5.00 kg,
Temperature 260 °C
22 g/10 min

@Load 11.0 lb,
Temperature 500 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
24 g/10 min

@Load 5.00 kg,
Temperature 260 °C
24 g/10 min

@Load 11.0 lb,
Temperature 500 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 115
115
ISO 2039-2
Hardness, H358/30 96.0 MPa
13900 psi
ISO 2039-1
Tensile Strength at Break 45.0 MPa
6530 psi
5 mm/min; ISO 527
45.0 MPa
6530 psi
50 mm/min; ISO 527
47.0 MPa
6820 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 55.0 MPa
7980 psi
5 mm/min; ISO 527
55.0 MPa
7980 psi
50 mm/min; ISO 527
57.0 MPa
8270 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break >= 50 %
>= 50 %
50 mm/min; ISO 527
100 %
100 %
Type I, 50 mm/min; ASTM D 638
100 %
100 %
5 mm/min; ISO 527
Elongation at Yield 4.0 %
4.0 %
50 mm/min; ISO 527
5.0 %
5.0 %
Type I, 50 mm/min; ASTM D 638
5.0 %
5.0 %
5 mm/min; ISO 527
Tensile Modulus 2.27 GPa
329 ksi
5 mm/min; ASTM D 638
2.40 GPa
348 ksi
1 mm/min; ISO 527
Flexural Yield Strength 80.0 MPa
11600 psi
2 mm/min; ISO 178
88.0 MPa
12800 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.30 GPa
334 ksi
1.3 mm/min, 50 mm span; ASTM D 790
2.30 GPa
334 ksi
2 mm/min; ISO 178
Izod Impact, Notched 4.80 J/cm

@Temperature -30.0 °C
8.99 ft-lb/in

@Temperature -22.0 °F
ASTM D 256
5.80 J/cm

@Temperature 23.0 °C
10.9 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Notched (ISO) 30.0 kJ/m²

@Temperature -30.0 °C
14.3 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
50.0 kJ/m²

@Temperature 23.0 °C
23.8 ft-lb/in²

@Temperature 73.4 °F
80*10*3; ISO 180/1A
Charpy Impact, Notched 3.00 J/cm²

@Temperature -30.0 °C
14.3 ft-lb/in²

@Temperature -22.0 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
5.00 J/cm²

@Temperature 23.0 °C
23.8 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
Impact Test 54.0 J

@Temperature 23.0 °C
39.8 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Taber Abrasion, mg/1000 Cycles 63

@Load 1.00 kg
63

@Load 2.20 lb
CS-17; SABIC Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
40.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
80.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
44.4 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
CTE, linear, Transverse to Flow 72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
40.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
80.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
44.4 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
Thermal Conductivity 0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 0.46 MPa (66 psi) 122 °C
252 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 102 °C
216 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
112 °C

@Thickness 3.20 mm
234 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Vicat Softening Point 126 °C
259 °F
Rate B/50; ISO 306
128 °C
262 °F
Rate B/120; ISO 306
130 °C
266 °F
Rate B/50; ASTM D 1525
UL RTI, Electrical 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical with Impact 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical without Impact 60.0 °C
140 °F
UL 746B
Flammability, UL94 HB

@Thickness 1.20 mm
HB

@Thickness 0.0472 in
UL 94
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
2nd value; UL 94
Oxygen Index 23 %
23 %
LOI; ISO 4589
Glow Wire Test 650 °C

@Thickness 1.00 mm
1200 °F

@Thickness 0.0394 in
Glow Wire Flammability Index; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 2.7

@Frequency 1.00e+6 Hz
2.7

@Frequency 1.00e+6 Hz
IEC 60250
2.8

@Frequency 50.0 - 60.0 Hz
2.8

@Frequency 50.0 - 60.0 Hz
IEC 60250
Dielectric Strength 17.0 kV/mm

@Thickness 3.20 mm
432 kV/in

@Thickness 0.126 in
in oil; IEC 60243-1
25.0 kV/mm

@Thickness 1.60 mm
635 kV/in

@Thickness 0.0630 in
in oil; IEC 60243-1
35.0 kV/mm

@Thickness 0.800 mm
889 kV/in

@Thickness 0.0315 in
in oil; IEC 60243-1
Dissipation Factor 0.0020

@Frequency 50.0 - 60.0 Hz
0.0020

@Frequency 50.0 - 60.0 Hz
IEC 60250
0.0070

@Frequency 1.00e+6 Hz
0.0070

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 250 V
250 V
IEC 60112
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES
IEC 60695-10-2