SABIC Innovative Plastics Cycoloy® C1000HF PC+ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycoloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycoloy® C1000HF PC+ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High flow PC+ABS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | ASTM D792 |
| Water Absorption | 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
ASTM D570 |
| Moisture Absorption at Equilibrium | 0.40 % | 0.40 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 7.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
7.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| 24 g/10 min @Load 5.00 kg, Temperature 260 °C |
24 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 57.0 MPa | 8270 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 80 % | 80 % | Type I, 50 mm/min; ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.48 GPa | 360 ksi | 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 91.0 MPa | 13200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.48 GPa | 360 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 5.34 J/cm | 10.0 ft-lb/in | ASTM D256 |
| 1.06 J/cm @Temperature -30.0 °C |
1.99 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Dart Drop, Total Energy | 40.0 J @Temperature -30.0 °C |
29.5 ft-lb @Temperature -22.0 °F |
ASTM D3763 |
| 54.0 J @Temperature 23.0 °C |
39.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 72.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C @Thickness 3.20 mm |
239 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.0 °C @Thickness 3.20 mm |
208 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne Versaflex™ 9555-9 Thermoplastic Elastomer (TPE)
- Nilit FRIANYL A63 KV25 Nylon 6.6 for injection molding, 25% glass ball reinforced
- Ravago Manufacturing Americas Enviramid™ N2335HL BK Post Consumer Recycle Nylon 6, 35% Glass Filled
- Saint-Gobain Chemfab® TCN® 1590 Leno Weave Nomex/Fiberglass Belting Material
- Elastomer Engineering Elastamide 150 Elastomer Modified RIM Nylon 6
- Diamond Polymers DIAMALOY FR530 PC/PBT Alloy, 30% Glass Filled Flame Retardant
- Fainplast Compounds FKT 0296/1 Flexible PVC, Insulation Lead Free
- Arlon LW201Xxx-P0 0.020" (0.508 mm) Self-Fusing Silicone Tape (Triangular, Unsupported) with Poly Interleave
- Fainplast Compounds PM 6510/K Flexible PVC, Lead Free
Copyright © lookpolymers.com All Rights Reserved