SABIC Innovative Plastics Cycolac® MG94 ABS

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycolac®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycolac® MG94 ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Superior flow, injection molding ABS. Good impact. For thin-wall applications.
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ASTM D792
Density 1.04 g/cc
0.0376 lb/in³
ISO 1183
Viscosity 172000 cP
172000 cP
Melt Viscosity, 240°C, 1000 sec-1; ASTM D3825
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0080 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 11.7 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 11.7 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 ASTM D1238
12 g/10 min

@Load 5.00 kg,
Temperature 220 °C
 12 g/10 min

@Load 11.0 lb,
Temperature 428 °F
 ISO 1133
42 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 42 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 113
113
ASTM D785
Tensile Strength at Break 35.0 MPa
5080 psi
Type I, 5 mm/min; ASTM D638
35.0 MPa
5080 psi
50 mm/min; ISO 527
Tensile Strength, Yield 46.0 MPa
6670 psi
Type I, 5 mm/min; ASTM D638
46.0 MPa
6670 psi
50 mm/min; ISO 527
Elongation at Break 18 %
18 %
Type I, 5 mm/min; ASTM D638
40 %
40 %
50 mm/min; ISO 527
Elongation at Yield 2.0 %
2.0 %
Type I, 5 mm/min; ASTM D638
2.3 %
2.3 %
50 mm/min; ISO 527
Tensile Modulus 2.45 GPa
355 ksi
1 mm/min; ISO 527
2.48 GPa
360 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 70.0 MPa
10200 psi
2 mm/min; ISO 178
79.0 MPa
11500 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.50 GPa
363 ksi
2 mm/min; ISO 178
2.62 GPa
380 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 2.40 J/cm
4.50 ft-lb/in
ASTM D256
0.800 J/cm

@Temperature -30.0 °C
 1.50 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Notched (ISO) 16.0 kJ/m²
7.61 ft-lb/in²
80*10*4; ISO 180/1A
7.00 kJ/m²

@Temperature -30.0 °C
 3.33 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 1.80 J/cm²
8.57 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 5.00 J

@Temperature -30.0 °C
 3.69 ft-lb

@Temperature -22.0 °F
 ASTM D3763
21.0 J

@Temperature 23.0 °C
 15.5 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 88.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
 49.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
88.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
 49.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 84.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 47.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
84.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 47.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 89.0 °C
192 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
95.0 °C

@Thickness 3.20 mm
 203 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 76.0 °C
169 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
82.0 °C

@Thickness 3.20 mm
 180 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Vicat Softening Point 98.0 °C
208 °F
Rate B/50; ASTM D1525
98.0 °C
208 °F
Rate B/50; ISO 306
100 °C
212 °F
Rate B/120; ISO 306
UL RTI, Electrical 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical with Impact 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical without Impact 60.0 °C
140 °F
UL 746B
Flammability, UL94 HB

@Thickness 1.52 mm
 HB

@Thickness 0.0598 in
 UL 94