- SABIC Innovative Plastics Cycolac® MG94 ABS (Europe-Africa-Middle East)
SABIC Innovative Plastics Cycolac® MG94 ABS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycolac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycolac® MG94 ABS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Superior flow, injection molding ABS. Good impact. For thin-wall applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.160 % | 0.160 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | on Tensile Bar; SABIC Method |
| Melt Index of Compound | 39 g/10 min @Load 10.0 kg, Temperature 220 °C |
39 g/10 min @Load 22.0 lb, Temperature 428 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 129 | 129 | ISO 2039-2 |
| Hardness, H358/30 | 95.0 MPa | 13800 psi | ISO 2039-1 |
| Tensile Strength at Break | 35.0 MPa | 5080 psi | 5 mm/min; ISO 527 |
| 35.0 MPa | 5080 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | 5 mm/min; ISO 527 |
| 45.0 MPa | 6530 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 35 % | 35 % | 5 mm/min; ISO 527 |
| 45 % | 45 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| 2.2 % | 2.2 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.40 GPa | 348 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 65.0 MPa | 9430 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.45 GPa | 355 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 18.0 kJ/m² | 8.57 ft-lb/in² | 80*10*4; ISO 180/1A |
| 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 2.30 J/cm² | 10.9 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 87.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
48.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 87.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
48.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| Vicat Softening Point | 99.0 °C | 210 °F | Rate B/50; ISO 306 |
| 100 °C | 212 °F | Rate B/120; ISO 306 | |
| Glow Wire Test | 650 °C @Thickness 3.20 mm |
1200 °F @Thickness 0.126 in |
IEC 60695-2-12 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® C4760 TPE, Transparent
- SABIC Innovative Plastics Cycoloy® CM8622 PC+ABS (Europe-Africa-Middle East)
- Metabolix Mirelâ„¢ P1004 Injection Molding Grade PHA Bioplastic
- Borealis Daplen™ EE115AE TPO Compound
- Valley Adhesives EM-220 Low Temperature Application Glue Stick
- Eagle Brass 18665 MSP1, Extra Hard
- DuPont Performance Polymers Zytel® 73G50HSLA BK416 Nylon 6 (Unverified Data**)
- Carmel Olefins CAPILENE® TU 75 AV Polypropylene Impact Copolymer
- Techmer ES Plastiblend® ABS 922 NAT
Copyright © lookpolymers.com All Rights Reserved