SABIC Innovative Plastics Cycolac® MG8000SR ABS

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycolac®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycolac® MG8000SR ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.06 g/cc
1.06 g/cc
ASTM D 792
Density 1.07 g/cc
0.0387 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 25 g/10 min

@Load 10.0 kg,
Temperature 220 °C
25 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ASTM D 1238
25 g/10 min

@Load 10.0 kg,
Temperature 220 °C
25 g/10 min

@Load 22.0 lb,
Temperature 428 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
33 g/10 min

@Load 5.00 kg,
Temperature 260 °C
33 g/10 min

@Load 11.0 lb,
Temperature 500 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell L 87
87
ISO 2039-2
Hardness, H358/30 100 MPa
14500 psi
ISO 2039-1
Hardness, Shore D 78
78
ASTM D 2240
Tensile Strength at Break 34.0 MPa
4930 psi
Type I, 5 mm/min; ASTM D 638
35.0 MPa
5080 psi
5 mm/min; ISO 527
37.0 MPa
5370 psi
Type I, 50 mm/min; ASTM D 638
39.0 MPa
5660 psi
50 mm/min; ISO 527
Tensile Strength, Yield 50.0 MPa
7250 psi
5 mm/min; ISO 527
51.0 MPa
7400 psi
Type I, 5 mm/min; ASTM D 638
56.0 MPa
8120 psi
50 mm/min; ISO 527
56.0 MPa
8120 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break 8.0 %
8.0 %
50 mm/min; ISO 527
9.0 %
9.0 %
Type I, 50 mm/min; ASTM D 638
10 %
10 %
Type I, 5 mm/min; ASTM D 638
10 %
10 %
5 mm/min; ISO 527
Elongation at Yield 2.8 %
2.8 %
Type I, 5 mm/min; ASTM D 638
2.8 %
2.8 %
5 mm/min; ISO 527
3.0 %
3.0 %
50 mm/min; ISO 527
3.0 %
3.0 %
Type I, 50 mm/min; ASTM D 638
Tensile Modulus 2.60 GPa
377 ksi
1 mm/min; ISO 527
2.65 GPa
384 ksi
5 mm/min; ASTM D 638
2.67 GPa
387 ksi
50 mm/min; ASTM D 638
Flexural Yield Strength 77.0 MPa
11200 psi
1.3 mm/min, 50 mm span; ASTM D 790
80.0 MPa
11600 psi
2 mm/min; ISO 178
Flexural Modulus 2.60 GPa
377 ksi
1.3 mm/min, 50 mm span; ASTM D 790
2.70 GPa
392 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.600 J/cm

@Temperature -30.0 °C
1.12 ft-lb/in

@Temperature -22.0 °F
ASTM D 256
0.800 J/cm

@Temperature 23.0 °C
1.50 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Notched (ISO) 7.00 kJ/m²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
12.0 kJ/m²

@Temperature 23.0 °C
5.71 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 0.800 J/cm²

@Temperature -30.0 °C
3.81 ft-lb/in²

@Temperature -22.0 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
1.30 J/cm²

@Temperature 23.0 °C
6.19 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 10.0 J
7.38 ft-lb
Multiaxial Impact; ISO 6603
25.0 J

@Temperature 23.0 °C
18.4 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 87.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
48.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
87.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
48.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 85.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
47.2 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
85.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
47.2 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 87.0 °C
189 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 77.0 °C
171 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
83.0 °C

@Thickness 3.20 mm
181 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Vicat Softening Point 89.0 °C
192 °F
Rate B/50; ASTM D 1525
91.0 °C
196 °F
Rate B/50; ISO 306
92.0 °C
198 °F
Rate B/120; ISO 306
98.0 °C
208 °F
Rate A/50; ISO 306
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
UL 94 by SABIC-IP
Descriptive Properties Value Comments
Pencil Hardness test, 1kgf HB
ASTM D 3363