SABIC Innovative Plastics Cycolac® MG38 ABS (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycolac®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycolac® MG38 ABS (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Very high impact ABS. Toughness/rigidity. Good fatigue resistance.
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ASTM D792
Density 1.04 g/cc
0.0376 lb/in³
ISO 1183
Viscosity 245000 cP
245000 cP
Melt Viscosity, 240°C, 1000 sec-1; ASTM D3825
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 3.7 g/10 min

@Load 3.80 kg,
Temperature 230 °C
3.7 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D1238
14 g/10 min

@Load 10.0 kg,
Temperature 220 °C
14 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 111
111
ASTM D785
Tensile Strength at Break 33.0 MPa
4790 psi
Type I, 5 mm/min; ASTM D638
34.0 MPa
4930 psi
50 mm/min; ISO 527
Tensile Strength, Yield 44.0 MPa
6380 psi
Type I, 5 mm/min; ASTM D638
47.0 MPa
6820 psi
50 mm/min; ISO 527
Elongation at Break 17 %
17 %
50 mm/min; ISO 527
26 %
26 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 2.1 %
2.1 %
Type I, 5 mm/min; ASTM D638
2.7 %
2.7 %
50 mm/min; ISO 527
Tensile Modulus 2.27 GPa
329 ksi
5 mm/min; ASTM D638
2.27 GPa
329 ksi
1 mm/min; ISO 527
Flexural Yield Strength 71.0 MPa
10300 psi
2 mm/min; ISO 178
72.0 MPa
10400 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.25 GPa
326 ksi
2 mm/min; ISO 178
2.34 GPa
339 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 3.70 J/cm
6.93 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 27.0 kJ/m²
12.8 ft-lb/in²
80*10*4; ISO 180/1A
9.00 kJ/m²

@Temperature -30.0 °C
4.28 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 2.80 J/cm²
13.3 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
1.00 J/cm²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 31.0 J

@Temperature 23.0 °C
22.9 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 88.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
49.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 86.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
48.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 95.0 °C

@Thickness 3.20 mm
203 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 81.0 °C
178 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
80.0 °C

@Thickness 3.20 mm
176 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 98.0 °C
208 °F
Rate B/50; ASTM D1525
98.0 °C
208 °F
Rate B/50; ISO 306
100 °C
212 °F
Rate B/120; ISO 306
UL RTI, Electrical 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical with Impact 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical without Impact 60.0 °C
140 °F
UL 746B
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
UL 94
Electrical Properties Metric English Comments
Arc Resistance 120 - 180 sec
120 - 180 sec
Tungsten; ASTM D495
Comparative Tracking Index >= 600 V
>= 600 V
UL 746A
Hot Wire Ignition, HWI 15 - 30 sec
15 - 30 sec
UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR 25.4 - 80.0 mm/min
1.00 - 3.15 in/min
UL 746A