SABIC Innovative Plastics Cycolac® INPBMAT ABS

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycolac®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycolac® INPBMAT ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Cross-linked SAN in styrenic matrix. Provides excellent gloss reduction properties. Maintains original polymer properties such as impact etc. Compatible with various polymer such as PVC and ABS. Can be used in low gloss ABS products at typical loading around 5PHR. Can be effectively compounded with ABS and other styrenic thermoplastics in molded, extruded or calendered applications to provide excellent gloss reduction properties without losing other physical performance.
Physical Properties Metric English Comments
Specific Gravity 1.07 g/cc
1.07 g/cc
ASTM D792
Density 1.07 g/cc
0.0387 lb/in³
ISO 1183
Mechanical Properties Metric English Comments
Flexural Yield Strength 33.0 MPa
4790 psi
1.3 mm/min, 50 mm span; ASTM D790
38.0 MPa
5510 psi
2 mm/min; ISO 178
Flexural Modulus 3.40 GPa
493 ksi
2 mm/min; ISO 178
3.70 GPa
537 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.180 J/cm
0.337 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 2.00 kJ/m²
0.952 ft-lb/in²
80*10*4; ISO 180/1A
1.00 kJ/m²

@Temperature -30.0 °C
0.476 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 94.0 °C

@Thickness 3.20 mm
201 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 87.0 °C
189 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
86.0 °C

@Thickness 3.20 mm
187 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 100 °C
212 °F
Rate B/50; ISO 306
102 °C
216 °F
Rate B/120; ISO 306