SABIC Innovative Plastics Cycolac® INP581 ABS+SAN
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycolac® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycolac® INP581 ABS+SAN.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High flow, low molecular weight SAN. Can be used as compounding additives for polymer blends. Can be blended with high rubber graft modifier resins to produce customized ABS properties. Suitable for direct weather exposure. Provides excellent flow for demanding injection molding applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Density | 1.07 g/cc | 0.0387 lb/in³ | ISO 1183 |
| Melt Flow | 37.7 g/10 min @Load 3.80 kg, Temperature 230 °C |
37.7 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| 98 g/10 min @Load 10.0 kg, Temperature 220 °C |
98 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength at Break | 60.0 MPa | 8700 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 1.9 % | 1.9 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 1.5 % | 1.5 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 4.08 GPa | 592 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 36.0 MPa | 5220 psi | 2 mm/min; ISO 178 |
| 66.0 MPa | 9570 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 3.44 GPa | 499 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 3.52 GPa | 511 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.230 J/cm | 0.431 ft-lb/in | ASTM D256 |
| 0.120 J/cm @Temperature -30.0 °C |
0.225 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 1.00 kJ/m² | 0.476 ft-lb/in² | 80*10*4; ISO 180/1A |
| 1.00 kJ/m² @Temperature -30.0 °C |
0.476 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.100 J/cm² | 0.476 ft-lb/in² | ISO 179/2C |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C @Thickness 3.20 mm |
207 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 86.0 °C @Thickness 3.20 mm |
187 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 102 °C | 216 °F | Rate B/50; ISO 306 |
| 104 °C | 219 °F | Rate B/120; ISO 306 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Yellow Index | 1.0 % | 1.0 % | ASTM D1925 |