SABIC Innovative Plastics Cycolac® INP572 ABS+SAN

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycolac®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycolac® INP572 ABS+SAN.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High molecular weight SAN, functions as a carrier resin for color concentrates. Can be used as compounding additives for polymer blends. Can be blended with high rubber graft modifier resins to produce customized ABS properties. Suitable for direct weather exposure. Provides excellent melt strength for extrusion, blow molding, or thermoforming applications
Physical Properties Metric English Comments
Specific Gravity 1.08 g/cc
1.08 g/cc
ASTM D792
Density 1.08 g/cc
0.0390 lb/in³
ISO 1183
Melt Flow 5.8 g/10 min

@Load 3.80 kg,
Temperature 230 °C
5.8 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D1238
16 g/10 min

@Load 10.0 kg,
Temperature 220 °C
16 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ISO 1133
Mechanical Properties Metric English Comments
Flexural Yield Strength 92.0 MPa
13300 psi
2 mm/min; ISO 178
134 MPa
19400 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 3.46 GPa
502 ksi
2 mm/min; ISO 178
3.90 GPa
566 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.460 J/cm
0.862 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 3.00 kJ/m²
1.43 ft-lb/in²
80*10*4; ISO 180/1A
2.00 kJ/m²

@Temperature -30.0 °C
0.952 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact Unnotched 0.100 J/cm²
0.476 ft-lb/in²
ISO 179/2C
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 95.0 °C

@Thickness 3.20 mm
203 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 87.0 °C
189 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
85.0 °C

@Thickness 3.20 mm
185 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 102 °C
216 °F
Rate B/50; ISO 306
105 °C
221 °F
Rate B/120; ISO 306