Material Notes:
Flame retardant ABS (non-PBBE additive). Good property/toughness. Excellent moldability. UL94 V-0/5VA rated.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Viscosity 290000 cP
290000 cP
Melt Viscosity, 200°C, 1000 sec-1; ASTM D3825
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 4.0 g/10 min

@Load 3.80 kg,
Temperature 230 °C
4.0 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D1238
10 g/10 min

@Load 5.00 kg,
Temperature 220 °C
10 g/10 min

@Load 11.0 lb,
Temperature 428 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 35.0 MPa
5080 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 41.0 MPa
5950 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 9.0 %
9.0 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 2.3 %
2.3 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 2.34 GPa
339 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 71.0 MPa
10300 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.72 GPa
395 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 2.13 J/cm
3.99 ft-lb/in
ASTM D256
Dart Drop, Total Energy 33.0 J

@Temperature 23.0 °C
24.3 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 84.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
47.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 86.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
48.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 82.0 °C

@Thickness 3.20 mm
180 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 70.0 °C

@Thickness 3.20 mm
158 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 86.0 °C
187 °F
Rate B/50; ASTM D1525
UL RTI, Electrical 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical with Impact 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical without Impact 60.0 °C
140 °F
UL 746B
Flammability, UL94 V-0

@Thickness 1.49 mm
V-0

@Thickness 0.0587 in
UL 94
5VA

@Thickness 2.48 mm
5VA

@Thickness 0.0976 in
UL 94
Electrical Properties Metric English Comments
Arc Resistance 0.00 - 60 sec
0.00 - 60 sec
Tungsten; ASTM D495
Comparative Tracking Index 250 - 400 V
250 - 400 V
UL 746A
Hot Wire Ignition, HWI 15 - 30 sec
15 - 30 sec
UL 746A
High Amp Arc Ignition, HAI 0.00 - 15 arcs
0.00 - 15 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR >= 150 mm/min
>= 5.91 in/min
UL 746A