Rogers Corporation RT/duroid® 6010.2LM Ceramic-PTFE Composite Microwave Laminate

Category Polymer , Thermoplastic , Fluoropolymer , PTFE , Polytetrafluoroethylene (PTFE), Glass Filled, Molded
Manufacturer Rogers Corporation
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Rogers Corporation RT/duroid® 6010.2LM Ceramic-PTFE Composite Microwave Laminate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features:High dielectric constant for circuit size reductionLow loss - Ideal for operating at X-band or belowLow Z-axis expansion. Provides reliable plated through holes in multi-layer boardsTight dielectric constant and thickness control for repeatable circuit performanceCladding - EDC or rolled copper foil, also thick aluminum, brass or copper plate (one side)Lead-free process compatibleTypical Applications:Space Saving CircuitryPatch AntennasGround Radar Warning SystemsSatellite Communications SystemsPower AmplifiersAircraft Collision Avoidance SystemsInformation provided by Rogers Corporation.
Physical Properties Metric English Comments
Density 3.10 g/cc
0.112 lb/in³
ASTM D792
Moisture Absorption at Equilibrium 0.010 %

@Temperature 50.0 °C,
Time 173000 sec
0.010 %

@Temperature 122 °F,
Time 48.0 hour
0.05 in.; IPC-TM-650 2.6.2.1
Thickness 127 - 2540 microns
5.00 - 100 mil
Range of Standard Thicknesses
Deformation 0.26 %

@Pressure 7.00 MPa,
Temperature 50.0 °C
0.26 %

@Pressure 1020 psi,
Temperature 122 °F
Z direction; 24 hrs; ASTM D621
1.37 %

@Pressure 7.00 MPa,
Temperature 150 °C
1.37 %

@Pressure 1020 psi,
Temperature 302 °F
Z direction; 24 hrs; ASTM D621
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 13.0 MPa
1890 psi
Y direction; 0.1/min strain rate; ASTM D638
17.0 MPa
2470 psi
X direction; 0.1/min strain rate; ASTM D638
Elongation at Break 7.0 - 14 %
7.0 - 14 %
Y direction; 0.1/min strain rate; ASTM D638
9.0 - 15 %
9.0 - 15 %
X direction; 0.1/min strain rate; ASTM D638
Flexural Strength 32.0 MPa
4640 psi
Y direction, Condition A; ASTM D790
36.0 MPa
5220 psi
X direction, Condition A; ASTM D790
Flexural Modulus 3.751 GPa
544.0 ksi
Y direction, Condition A; ASTM D790
4.364 GPa
632.9 ksi
X direction, Condition A; ASTM D790
Compressive Yield Strength 47.0 MPa

@Strain 25.0 %
6820 psi

@Strain 25.0 %
Z direction; 0.05/min strain rate; ASTM D695
Compressive Modulus 2.144 GPa
311.0 ksi
Z direction; 0.05/min strain rate; ASTM D695
Peel Strength 2.16 kN/m
12.3 pli
Copper, after solder float; IPC-TM-650 2.4.8
Thermal Properties Metric English Comments
CTE, linear 24.0 µm/m-°C

@Temperature 0.000 - 100 °C
13.3 µin/in-°F

@Temperature 32.0 - 212 °F
X-Direction; 5°C/min; ASTM D3386
24.0 µm/m-°C

@Temperature 0.000 - 100 °C
13.3 µin/in-°F

@Temperature 32.0 - 212 °F
Y-Direction; 5°C/min; ASTM D3386
47.0 µm/m-°C

@Temperature 0.000 - 100 °C
26.1 µin/in-°F

@Temperature 32.0 - 212 °F
Z-Direction; 5°C/min; ASTM D3386
Specific Heat Capacity 1.00 J/g-°C
0.239 BTU/lb-°F
calculated
Thermal Conductivity 0.860 W/m-K

@Temperature 80.0 °C
5.97 BTU-in/hr-ft²-°F

@Temperature 176 °F
ASTM C518
Decomposition Temperature 500 °C
932 °F
TGA; ASTM D3850
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 5.00e+12 ohm-cm
5.00e+12 ohm-cm
Condition A; IPC 2.5.17.1
Surface Resistance 5.00e+12 ohm
5.00e+12 ohm
Condition A; IPC 2.5.17.1
Dielectric Constant 9.95 - 10.45

@Frequency 1.00e+10 Hz
9.95 - 10.45

@Frequency 1.00e+10 Hz
Z direction; IPC-TM-650 2.5.5.5
10.9

@Frequency 8.00e+9 - 4.00e+10 Hz
10.9

@Frequency 8.00e+9 - 4.00e+10 Hz
Differential Phase Length Method
Dissipation Factor 0.0023

@Frequency 1.00e+10 Hz
0.0023

@Frequency 1.00e+10 Hz
Z direction; IPC-TM-650 2.5.5.5
Descriptive Properties Value Comments
Thermal Coefficient of Dielectric Constant -425 ppm/°C
IPC-TM-650 2.5.5.5; 10 GHz; -50°C to 170°C; Z-Direction