Rogers Corporation RT/duroid® 6002 High Frequency Laminate

Category Polymer
Manufacturer Rogers Corporation
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Rogers Corporation RT/duroid® 6002 High Frequency Laminate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features:Low loss for excellent high frequency performanceTight dielectric constant and thickness controlExcellent electrical and mechanical propertiesExtremely low thermal coefficient of dielectric constantIn-plane expansion coefficient matched to copperLow Z-axis expansionLow outgassing; ideal for space applicationsCopper cladding - EDC or rolled foilLead-free process compatibleTypical Applications:Phase Array AntennasGround Based and Airborne Radar SystemsGlobal Positioning System AntennasPower BackplanesHigh Reliability Complex Multilayer CircuitsCommercial Airline Collision Avoidance SystemsBeam Forming NetworksInformation provided by Rogers Corporation.
Physical Properties Metric English Comments
Density 2.10 g/cc
0.0759 lb/in³
ASTM D792
Moisture Absorption at Equilibrium 0.020 %
0.020 %
D48/50; IPC-TM-650 2.6.2.1; ASTM D570
Thickness 127 - 3050 microns
5.00 - 120 mil
Range of Standard Thicknesses
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 6.90 MPa
1000 psi
X, Y direction; ASTM D638
Elongation at Break 7.3 %
7.3 %
X, Y direction; ASTM D638
Tensile Modulus 0.827 GPa
120 ksi
X, Y direction; ASTM D638
Compressive Modulus 2.482 GPa
360.0 ksi
Z direction; ASTM D638
Peel Strength 1.56 kN/m
8.90 pli
Copper; IPC-TM-650 2.4.8
Thermal Properties Metric English Comments
CTE, linear 16.0 µm/m-°C
8.89 µin/in-°F
X-Direction; TMA; 10°C/min; ASTM D3386; IPC-TM-650 2.4.41
16.0 µm/m-°C
8.89 µin/in-°F
Y-Direction; TMA; 10°C/min; ASTM D3386; IPC-TM-650 2.4.41
24.0 µm/m-°C
13.3 µin/in-°F
Z-Direction; TMA; 10°C/min; ASTM D3386; IPC-TM-650 2.4.41
Specific Heat Capacity 0.930 J/g-°C
0.222 BTU/lb-°F
calculated
Thermal Conductivity 0.600 W/m-K

@Temperature 80.0 °C
4.16 BTU-in/hr-ft²-°F

@Temperature 176 °F
ASTM C518
Decomposition Temperature 500 °C
932 °F
TGA; ASTM D3850
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
Condition A; ASTM D257
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
Condition A; ASTM D257
Dielectric Constant 2.9 - 2.98

@Frequency 1.00e+10 Hz
2.9 - 2.98

@Frequency 1.00e+10 Hz
Z direction; Process; IPC-TM-650 2.5.5.5
2.94

@Frequency 8.00e+9 - 4.00e+10 Hz
2.94

@Frequency 8.00e+9 - 4.00e+10 Hz
Design; Differential Phase Length Method
Dissipation Factor 0.0012

@Frequency 1.00e+10 Hz
0.0012

@Frequency 1.00e+10 Hz
Z direction; IPC-TM-650 2.5.5.5
Descriptive Properties Value Comments
Thermal Coefficient of Dielectric Constant 12 ppm/°C
IPC-TM-650 2.5.5.5; 10 GHz; 0°C to 100°C; Z-Direction