Rogers Corporation RO4535 Ceramic-Filled, Glass-Reinforced Hydrocarbon Laminate

Category Polymer , Thermoset
Manufacturer Rogers Corporation
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Rogers Corporation RO4535 Ceramic-Filled, Glass-Reinforced Hydrocarbon Laminate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The RO4500™ Series Cost Performance Antenna Grade Laminates are ceramic-filled, glass-reinforced hydrocarbon based materials that provides the controlled dielectric constant, low loss performance and excellent passive intermodulation response required for mobile infrastructure microstrip antenna applications.Features:Loss range (0.0020 to 0.0037)Dk range (3.3 to 3.5)Low PIM responseThermoset resin systemExcellent dimensional stabilityUniform mechanical propertiesHigh thermal conductivityLead-free process compatibleBenefits:Wide range of application use, including Cellular infrastructure base station antennas and WiMAX antenna networksCompatible with standard PCB fabricationGreater yield on larger panel sizesRobust handling and long life in use with thin materialsImproved power handlingInformation provided by Rogers Corporation.
Physical Properties Metric English Comments
Density 1.80 g/cc
0.0650 lb/in³
ASTM D792
Moisture Absorption at Equilibrium 0.050 %
0.050 %
D48/50; IPC-TM-650 2.6.2.1; ASTM D570
Mechanical Properties Metric English Comments
Peel Strength 1.23 kN/m
7.00 pli
Copper; 1 oz. EDC post Solder Float; IPC-TM-650 2.4.8
Thermal Properties Metric English Comments
CTE, linear 14.0 µm/m-°C

@Temperature -55.0 - 288 °C
7.78 µin/in-°F

@Temperature -67.0 - 550 °F
X-Direction; ASTM D3386-94
16.0 µm/m-°C

@Temperature -55.0 - 288 °C
8.89 µin/in-°F

@Temperature -67.0 - 550 °F
Y-Direction; ASTM D3386-94
35.0 µm/m-°C

@Temperature -55.0 - 288 °C
19.4 µin/in-°F

@Temperature -67.0 - 550 °F
Z-Direction; ASTM D3386-94
Thermal Conductivity 0.500 W/m-K

@Temperature 80.0 °C
3.47 BTU-in/hr-ft²-°F

@Temperature 176 °F
ASTM C518
Glass Transition Temp, Tg >= 280 °C
>= 536 °F
TGA, Condition A; IPC-TM-650 2.4.24
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Dielectric Constant 3.42 - 3.58

@Frequency 1.00e+10 Hz
3.42 - 3.58

@Frequency 1.00e+10 Hz
Z direction; IPC-TM-650 2.5.5.5
Dielectric Strength >= 19.7 kV/mm

@Thickness 0.510 mm
>= 500 kV/in

@Thickness 0.0201 in
Z Direction; IPC-TM-650 2.5.6.2
Dissipation Factor 0.0032

@Frequency 2.50e+9 Hz
0.0032

@Frequency 2.50e+9 Hz
Z direction; IPC-TM-650 2.5.5.5
0.0037

@Frequency 1.00e+10 Hz
0.0037

@Frequency 1.00e+10 Hz
Z direction; IPC-TM-650 2.5.5.5
Descriptive Properties Value Comments
Dimensional Stability < 0.5 mm/m
X, Y directions; after etch; IPC-TM-650, 2.4.39A